PA6 Durethan® BKV50 LANXESS GERMANY

108

So sánh
Xem giá

Bảng thông số kỹ thuật

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ISO 180/1A	17 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap -30°C	ISO 180/1A	15 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch -30°C	ISO 179/1eU	95 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch 23°C	ISO 179/1eU	100 kJ/m²
Bending modulus	Bending modulus 23°C	ISO 178	15000 Mpa
bending strength	bending strength 23°C	ISO 178	340 Mpa
Tensile modulus	Tensile modulus 23°C	ISO 527-2	16200 Mpa
Elongation at Break	Elongation at Break 23°C	ISO 527-2	2.70 %
tensile strength	tensile strength 23°C	ISO 527-2	215 Mpa
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength -30°C	ISO 180/1U	85 kJ/m²
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength 23°C	ISO 180/1U	85 kJ/m²

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD	ISO 11359-2	9E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD	ISO 11359-2	1.2E-05 cm/cm/°C
Vicat softening temperature	Vicat softening temperature Melting Temperature	ISO 11357-3	222 °C
Hot deformation temperature	Hot deformation temperature 1.80MPaAnnealed	ISO 75-2/Af	210 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 0.45MPaUnannealed	ISO 75-2/Bf	220 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Shrinkage rate	Shrinkage rate TD2.0mm	ISO 294-4	0.60 %
Shrinkage rate	Shrinkage rate MD2.0mm	ISO 294-4	0.19 %

Physical properties

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Shrinkage rate

TD2.0mm

ISO 294-4

0.60 %

Shrinkage rate

MD2.0mm

ISO 294-4

0.19 %

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Dissipation factor	Dissipation factor 相对漏电起痕指数	IEC 60112	400 V
	Dissipation factor	Dissipation factor 23°C	IEC 60250	0.017 1MHz
	Dissipation factor	Dissipation factor	Dissipation factor 23°C	IEC 60250	0.014 100HZ
Dielectric constant	Dielectric constant 23°C	IEC 60250	4.20 1MHz
Dielectric constant	Dielectric constant	Dielectric constant 23°C	IEC 60250	4.70 100HZ
Dielectric strength	Dielectric strength 1.00mm	IEC 60243-1	35 KV/mm
Volume resistivity	Volume resistivity	IEC 60093	7E+14 Ω.cm

hardness	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Ball Pressure Test	Ball Pressure Test	ISO 2039-1	232 Mpa

hardness

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Ball Pressure Test

ISO 2039-1

232 Mpa

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.