| impact performance | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Impact strength of simply supported beam without notch | Impact strength of simply supported beam without notch -30°C | ISO 179/1eU | 45 kJ/m² |
| Impact strength of simply supported beam without notch | Impact strength of simply supported beam without notch 23°C | ISO 179/1eU | 55 kJ/m² |
| Multi axis Instrumented Peak Impact Force | Multi axis Instrumented Peak Impact Force 23°C | ISO 6603-2 | 1000 N |
| Multi axis Instrumented Peak Impact Force | Multi axis Instrumented Peak Impact Force -30°C | ISO 6603-2 | 900 N |
| Multi axis Instrumented Impact Energy | Multi axis Instrumented Impact Energy 23°C | ISO 6603-2 | 3.00 J |
| Multi axis Instrumented Impact Energy | Multi axis Instrumented Impact Energy -30°C | ISO 6603-2 | 1.90 J |
| Suspended wall beam without notch impact strength | Suspended wall beam without notch impact strength 23°C | ISO 180/1U | 50 kJ/m² |
| Suspended wall beam without notch impact strength | Suspended wall beam without notch impact strength -30°C | ISO 180/1U | 45 kJ/m² |
| flammability | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| UL flame retardant rating | UL flame retardant rating 0.40mm | UL 94 | V-0 |
| BurningBehavior | BurningBehavior | ISO 3795 | passed |
| Hot filament ignition temperature | Hot filament ignition temperature 3.0mm | IEC 60695-2-13 | 850 °C |
| Hot filament ignition temperature | Hot filament ignition temperature 1.5mm | IEC 60695-2-13 | 775 °C |
| Hot filament ignition temperature | Hot filament ignition temperature 0.8mm | IEC 60695-2-13 | 775 °C |
| Hot filament ignition temperature | Hot filament ignition temperature 0.40mm | IEC 60695-2-13 | 850 °C |
| Burning wire flammability index | Burning wire flammability index 3.0mm | IEC 60695-2-12 | 960 °C |
| Burning wire flammability index | Burning wire flammability index 1.5mm | IEC 60695-2-12 | 960 °C |
| Burning wire flammability index | Burning wire flammability index 0.8mm | IEC 60695-2-12 | 960 °C |
| Burning wire flammability index | Burning wire flammability index 0.40mm | IEC 60695-2-12 | 960 °C |
| UL flame retardant rating | UL flame retardant rating 1.0mm | UL 94 | V-0 |
| UL flame retardant rating | UL flame retardant rating 3.0mm | UL 94 | V-0 |
| mechanical properties | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Bending modulus | Bending modulus 23°C | ISO 178/A | 10000 Mpa |
| bending strength | bending strength 23°C | ISO 178/A | 230 Mpa |
| Bending strain | Bending strain 23°C | ISO 178/A | 2.5 % |
| Tensile modulus | Tensile modulus 23°C | ISO 527-2/1 | 11000 Mpa |
| tensile strength | tensile strength Break,23°C | ISO 527-2/5 | 150 Mpa |
| Tensile strain | Tensile strain Break,23°C | ISO 527-2/5 | 2.3 % |
| thermal performance | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Linear coefficient of thermal expansion | Linear coefficient of thermal expansion TD：23to55°C | ISO 11359-2 | 9E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | Linear coefficient of thermal expansion MD：23to55°C | ISO 11359-2 | 2E-05 cm/cm/°C |
| Melting temperature | Melting temperature | ISO 11357-3 | 222 °C |
| Vicat softening temperature | Vicat softening temperature | ISO 306/B120 | 205 °C |
| Hot deformation temperature | Hot deformation temperature 1.8MPa,Unannealed | ISO 75-2/A | 205 °C |
| Hot deformation temperature | Hot deformation temperature 0.45MPa,Unannealed | ISO 75-2/B | 215 °C |
| Physical properties | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Shrinkage rate | Shrinkage rate TD:280°C,2.00mm2 | ISO 2577 | 0.60 % |
| Shrinkage rate | Shrinkage rate TD:120°C,4hr,2.00mm3 | ISO 2577 | 0.10 % |
| Shrinkage rate | Shrinkage rate MD:280°C,2.00mm2 | ISO 2577 | 0.30 % |
| Shrinkage rate | Shrinkage rate MD:120°C,4hr,2.00mm3 | ISO 2577 | 0.10 % |
| Electrical performance | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Compared to the anti leakage trace index | Compared to the anti leakage trace index SolutionA | IEC 60112 | PLC 1 |
| Volume resistivity | Volume resistivity 23°C | IEC 60093 | 3.4E+14 ohms·cm |
| Surface resistivity | Surface resistivity | IEC 60093 | 4.1E+13 ohms |
| Supplementary Information | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| ISO Shortcut | ISO Shortcut | ISO 1874 | PA6.GFHR.14-110.GF25 |