thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed	ASTMD648	130 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed	ASTMD648	78.0 °C
Vicat softening temperature	Vicat softening temperature --	ASTMD15251	155 °C
Vicat softening temperature	Vicat softening temperature	Vicat softening temperature --	ASTMD15252	100 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
density	density	ASTMD792	2.15 g/cm³
melt mass-flow rate	melt mass-flow rate 230°C/2.16kg	ASTMD1238	4.0 g/10min
Shrinkage rate	Shrinkage rate MD	ASTM D955	0.50 %
Shrinkage rate	Shrinkage rate	Shrinkage rate TD	ASTM D955	0.50 %

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Compared to the anti leakage trace index	Compared to the anti leakage trace index SolutionA	IEC 60112	PLC 0

Electrical performance

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Compared to the anti leakage trace index

SolutionA

IEC 60112

PLC 0

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.