SMA XIRAN® SG260 POLYSCOPE HOLLAND

So sánh

Bảng thông số kỹ thuật

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap -40°C	ISO 180/A	8.0 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ISO 180/A	9.0 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength -40°C	ISO 179/1eA	8.0 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C	ISO 179/1eA	9.0 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch -40°C	ISO 179/1eU	34 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch 23°C	ISO 179/1eU	30 kJ/m²

flammability	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
UL flame retardant rating	UL flame retardant rating	UL 94	HB

flammability

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

UL flame retardant rating

UL 94

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Tensile modulus	Tensile modulus	ISO 527-2	8500 MPa
tensile strength	tensile strength Break	ISO 527-2	90.0 MPa
Tensile strain	Tensile strain Break	ISO 527-2	2.0 %
Bending modulus	Bending modulus	ISO 178	8500 MPa
bending strength	bending strength	ISO 178	150 MPa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed	ISO 75-2/A	120 °C
Vicat softening temperature	Vicat softening temperature	ISO 306/B	118 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD：-30to80°C	ASTM D696	2.9E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD：-30to80°C	ASTM D696	4.7E-05 cm/cm/°C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
density	density	ISO 1183	1.28 g/cm³
melt mass-flow rate	melt mass-flow rate 220°C/10.0kg	ISO 1133	2.5 g/10min
Spiral flow length	Spiral flow length	Internal Method	26.0 cm
Shrinkage rate	Shrinkage rate TD	Internal Method	0.50 %
Shrinkage rate	Shrinkage rate	Shrinkage rate MD	Internal Method	0.20 %
Water absorption rate	Water absorption rate Equilibrium,23°C,50%RH	ASTM D570	0.20 %

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.