mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
tensile strength	tensile strength	ASTM D638/ISO 527	420(5950) kg/cm²(MPa)[Lb/in²]
elongation	elongation	ASTM D638/ISO 527	30 %
Rockwell hardness	Rockwell hardness	ASTM D785	R-108
Bending modulus	Bending modulus	ASTM D790/ISO 178	2.2(3.1) kg/cm²(MPa)[Lb/in²]
bending strength	bending strength	ASTM D790/ISO 178	620(8800) kg/cm²(MPa)[Lb/in²]
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	ASTM D256/ISO 179	33(6.1) kg·cm/cm(J/M)ft·lb/in
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	ASTM D256/ISO 179	37.5(6.9) kg·cm/cm(J/M)ft·lb/in
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 1/4"	ASTM D-256	35 kg.cm/cm
bending strength	bending strength	ASTM D-790	620 kg/cm2
Elongation at Break	Elongation at Break	ASTM D-790	40 %
Bending modulus	Bending modulus	ASTM D-790	2.1 104kg/cm2
Rockwell hardness	Rockwell hardness	ASTM D-785	102 R
tensile strength	tensile strength	ASTM D-638	390 kg/cm2
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 1/8"	ASTM D-256	40 kg.cm/cm

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Combustibility (rate)	Combustibility (rate)	UL 94	1.6mm
Hot deformation temperature	Hot deformation temperature HDT	ASTM D648/ISO 75	97(207) ℃（℉）
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature HDT	ASTM D648/ISO 75	86(187) ℃（℉）
Vicat softening temperature	Vicat softening temperature	ASTM D1525/ISO R306	103(217) ℃（℉）
Hot deformation temperature	Hot deformation temperature Annealed	ASTM D-648	97(207) ℃(°F)
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature Unannealed	ASTM D-648	87(189) ℃(°F)
Vicat softening temperature	Vicat softening temperature	ASTM D-1525	103(217) ℃(°F)
Combustibility	Combustibility	File NO.E196075	1/16"HB

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
density	density	ASTM D792/ISO 1183	1.03
melt mass-flow rate	melt mass-flow rate	ASTM D1238/ISO 1133	0.8 g/10min
melt mass-flow rate	melt mass-flow rate	ASTM D1238/ISO 1133	9 g/10min

Physical properties

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

density

ASTM D792/ISO 1183

1.03

melt mass-flow rate

ASTM D1238/ISO 1133

0.8 g/10min

melt mass-flow rate

ASTM D1238/ISO 1133

9 g/10min

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.