elastomer	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Permanent compression deformation	Permanent compression deformation 125°C,70hr	ISO 815	50 %
	Permanent compression deformation	Permanent compression deformation 70°C,22hr	ISO 815	34 %
	Permanent compression deformation	Permanent compression deformation	Permanent compression deformation 23°C,22hr	ISO 815	24 %
tear strength	tear strength 横向Flow	ISO 34-1	30 kN/m
elongation	elongation Flow:Break	ISO 37	410 %
elongation	elongation	elongation 横向Flow:Break	ISO 37	490 %
tensile strength	tensile strength Flow:Break	ISO 37	5.40 Mpa
	tensile strength	tensile strength 横向Flow:Break	ISO 37	6.10 Mpa
		tensile strength	tensile strength Flow:100%Strain	ISO 37	3.50 Mpa
		tensile strength	tensile strength	tensile strength 横向Flow:100%Strain	ISO 37	2.80 Mpa

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Friction coefficient	Friction coefficient	ASTM D1894	0.40to0.50

mechanical properties

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Friction coefficient

ASTM D1894

0.40to0.50

hardness	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Shore hardness	Shore hardness ShoreA,5Sec,Injection	ISO 868	75
Shore hardness	Shore hardness ShoreA,5Sec,挤塑	ISO 868	73

hardness

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Shore hardness

ShoreA,5Sec,Injection

ISO 868

Shore hardness

ShoreA,5Sec,挤塑

ISO 868

aging	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Change rate of tensile strength in air	Change rate of tensile strength in air 100%Strain150°C,168hr，Across Flow	ISO 188	0.0 %
Tensile stress change rate	Tensile stress change rate 135°C,1008hr，Break	ISO 188	-20 %
Tensile stress change rate	Tensile stress change rate	Tensile stress change rate 150°C,168hr，Break	ISO 188	-25 %
Change rate of tensile strength in air	Change rate of tensile strength in air 150°C,168hr，Across Flow	ISO 188	-25 %
	Change rate of tensile strength in air	Change rate of tensile strength in air 100%Strain135°C,1008hr，Across Flow	ISO 188	5.0 %
	Change rate of tensile strength in air	Change rate of tensile strength in air	Change rate of tensile strength in air 135°C,1008hr，Across Flow	ISO 188	-15 %
Volume change	Volume change 125°C,70hr,在IRM903油中	ISO 1817	70 %
Change rate of hardness (Shore) in the air	Change rate of hardness (Shore) in the air ShoreA,150°C,168hr	ISO 188	-3.0
Change rate of hardness (Shore) in the air	Change rate of hardness (Shore) in the air	Change rate of hardness (Shore) in the air ShoreA,135°C,1008hr	ISO 188	0.0

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.