mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
bending strength	bending strength Yield, 50.0 mm Span	ASTM D790	72.0 Mpa
Bending modulus	Bending modulus 50.0 mm Span	ASTM D790	2060 Mpa
elongation	elongation Break	ASTM D638	150 %
elongation	elongation	elongation Yield	ASTM D638	8.6 %
tensile strength	tensile strength Break	ASTM D638	44.0 Mpa
tensile strength	tensile strength	tensile strength Yield	ASTM D638	50.0 Mpa
Tensile modulus	Tensile modulus	ASTM D638	2130 Mpa

injection	Điều kiện kiểm tra	Kết quả kiểm tra
Temperature in the middle of the barrel	Temperature in the middle of the barrel	255 to 290 °C
Temperature at the rear of the barrel	Temperature at the rear of the barrel	250 to 280 °C
Suggested injection volume	Suggested injection volume	30 to 80 %
Suggested maximum moisture content	Suggested maximum moisture content	0.020 %
drying time	drying time	3.0 to 4.0 hr
drying temperature	drying temperature	100 to 105 °C
Temperature at the front of the material cylinder	Temperature at the front of the material cylinder	255 to 290 °C
Spray nozzle temperature	Spray nozzle temperature	260 to 290 °C
Processing (melt) temperature	Processing (melt) temperature	260 to 290 °C
Mold temperature	Mold temperature	75 to 100 °C
Back pressure	Back pressure	0.300 to 0.700 Mpa
Screw speed	Screw speed	40 to 70 rpm
Exhaust hole depth	Exhaust hole depth	0.038 to 0.076 mm

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
thermal conductivity	thermal conductivity	ASTM C177	0.20 W/m/K
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion Across Flow : -40 to 40°C	ASTM E831	9.0E-5 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion Flow : -40 to 40°C	ASTM E831	7.2E-5 cm/cm/°C
Vicat softening temperature	Vicat softening temperature	ASTM D15255	111 °C
Hot deformation temperature	Hot deformation temperature 1.8 MPa, Unannealed, 3.20 mm	ASTM D648	98.0 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 0.45 MPa, Unannealed, 3.20 mm	ASTM D648	115 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Water absorption rate	Water absorption rate 24 hr	ASTM D570	0.10 %
Shrinkage rate	Shrinkage rate Across FlowFlow : 3.20 mm	Internal Method	0.50 - 0.70 %
Shrinkage rate	Shrinkage rate	Shrinkage rate Flow : 3.20 mm	Internal Method	0.50 - 0.80 %
melt mass-flow rate	melt mass-flow rate 260°C/5.0 kg	ASTM D1238	14 g/10 min

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.