PP EP1X35F Dushanzi Petrochemical

So sánh

Bảng thông số kỹ thuật

Other performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
fisheye	fisheye 0.7-1.5		合格｜- pa
	fisheye	fisheye 0.7-1.5		一等｜- pa
		fisheye	fisheye 0.7-1.5		优等｜≤30 pa
			fisheye	fisheye 1.5-2.5		合格｜- pa
				fisheye	fisheye 1.5-2.5		一等｜- pa
					fisheye	fisheye 1.5-2.5		优等｜≤3 pa
						fisheye	fisheye ≥2.5		合格｜- pa
							fisheye	fisheye ≥2.5		一等｜- pa
							fisheye	fisheye	fisheye ≥2.5		优等｜≤0 pa
Titanium content	Titanium content		合格｜- ppm
Isotropy	Isotropy		一等｜≥94.5 %
Isotropy	Isotropy	Isotropy		优等｜≥94.5 %
fisheye	fisheye 0.2-0.7		一等｜- pa
fisheye	fisheye	fisheye 0.2-0.7		优等｜≤100 pa
ash content	ash content		合格｜≤400 ppm
ash content	ash content	ash content		一等｜≤300 ppm
Isotropy	Isotropy		合格｜≥94.5 %
Chlorine content	Chlorine content		优等｜≤55 ppm
	Chlorine content	Chlorine content		一等｜- ppm
	Chlorine content	Chlorine content	Chlorine content		合格｜- ppm
ash content	ash content		优等｜≤200 ppm
fisheye	fisheye 0.2-0.7		合格｜- pa
Huangdu Index	Huangdu Index		优等｜≤4 ppm
	Huangdu Index	Huangdu Index		一等｜- ppm
	Huangdu Index	Huangdu Index	Huangdu Index		合格｜- ppm
Titanium content	Titanium content		优等｜≤3 ppm
Titanium content	Titanium content	Titanium content		一等｜- ppm

Basic Performance	Điều kiện kiểm tra	Kết quả kiểm tra
melt mass-flow rate	melt mass-flow rate	合格｜5.5-12.5 g/10min
melt mass-flow rate	melt mass-flow rate	优等｜7.0-10.0 g/10min
melt mass-flow rate	melt mass-flow rate	一等｜6.85-11.5 g/10min

Basic Performance

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

melt mass-flow rate

合格｜5.5-12.5 g/10min

melt mass-flow rate

优等｜7.0-10.0 g/10min

melt mass-flow rate

一等｜6.85-11.5 g/10min

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
tensile strength	tensile strength Yield		合格｜25.5 MPa
	tensile strength	tensile strength Yield		一等｜26.5 MPa
	tensile strength	tensile strength	tensile strength Yield		优等｜27.5 MPa
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23℃		优等｜34.3 j/m
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23℃		一等｜17.6 j/m
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23℃		合格｜15.7 j/m
Bending modulus	Bending modulus		优等｜0.98 Gpa
	Bending modulus	Bending modulus		一等｜0.98 Gpa
	Bending modulus	Bending modulus	Bending modulus		合格｜- Gpa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot deformation temperature	Hot deformation temperature HDT		合格｜- ℃
	Hot deformation temperature	Hot deformation temperature HDT		一等｜- ℃
	Hot deformation temperature	Hot deformation temperature	Hot deformation temperature HDT		优等｜77 ℃
Vicat softening temperature	Vicat softening temperature		合格｜- ℃
	Vicat softening temperature	Vicat softening temperature		一等｜- ℃
	Vicat softening temperature	Vicat softening temperature	Vicat softening temperature		优等｜138 ℃

Physical properties	Điều kiện kiểm tra	Kết quả kiểm tra
turbidity	turbidity	优等｜≤2 %
turbidity	turbidity	一等｜≤2 %
turbidity	turbidity	合格｜≤5 %

Physical properties

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

turbidity

优等｜≤2 %

turbidity

一等｜≤2 %

turbidity

合格｜≤5 %

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.