TPC-ET Hytrel® 6356 DUPONT USA

So sánh

Bảng thông số kỹ thuật

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Charpy Notched Impact Strength	Charpy Notched Impact Strength -30°C	ISO 179/1eA	25 kJ/m²
	Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C,Partial Break	ISO 179/1eA	120 kJ/m²
	Charpy Notched Impact Strength	Charpy Notched Impact Strength	Charpy Notched Impact Strength -40°C	ISO 179/1eA	15 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap -40°C	ISO 180/1A	19 kJ/m²
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ISO 180/1A	81 kJ/m²
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ISO 8256/1	300 kJ/m²

flammability	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Fogging-G-value	Fogging-G-value condensate	ISO 6452	1E-04 g
FMVSS flammability	FMVSS flammability	FMVSS302	SE
Extreme Oxygen Index	Extreme Oxygen Index	ISO 4589-2	21 %
UL flame retardant rating	UL flame retardant rating 3.0mm	IEC 60695-11-10,-20	HB
	UL flame retardant rating	UL flame retardant rating 1.5mm	IEC 60695-11-10,-20	HB
		UL flame retardant rating	UL flame retardant rating 3.0mm	UL 94	HB
		UL flame retardant rating	UL flame retardant rating	UL flame retardant rating 1.5mm	UL 94	HB

elastomer	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
tear strength	tear strength 横向Flow	ISO 34-1	150 kN/m
tear strength	tear strength Flow	ISO 34-1	160 kN/m

elastomer

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

tear strength

横向Flow

ISO 34-1

150 kN/m

tear strength

Flow

ISO 34-1

160 kN/m

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Nominal tensile fracture strain	Nominal tensile fracture strain	ISO 527-2	500 %
Tensile creep modulus	Tensile creep modulus 1hr	ISO 899-1	248 MPa
Tensile creep modulus	Tensile creep modulus	Tensile creep modulus 1000hr	ISO 899-1	182 MPa
Tensile strain	Tensile strain Break	ISO 527-2	>300 %
Tensile strain	Tensile strain	Tensile strain Yield	ISO 527-2	31 %
Tensile modulus	Tensile modulus	ISO 527-2	280 MPa
tensile strength	tensile strength Yield	ISO 527-2	20.0 MPa
Bending modulus	Bending modulus	ISO 178	290 MPa
Wear resistance	Wear resistance	ISO 4649	110 mm³
tensile strength	tensile strength Break	ISO 527-2	43.0 MPa
	tensile strength	tensile strength 5.0%Strain	ISO 527-2	12.0 MPa
		tensile strength	tensile strength 10%Strain	ISO 527-2	15.0 MPa
			tensile strength	tensile strength 50%Strain	ISO 527-2	18.8 MPa
			tensile strength	tensile strength	tensile strength 100%Strain	ISO 527-2	19.0 MPa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD：-40to23°C	ISO 11359-2	1.5E-04 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD：EffectiveThermalDiffusivity	ISO 11359-2	5.44E-08 m²/s
Melting temperature	Melting temperature	ISO 11357-3	210 °C
Vicat softening temperature	Vicat softening temperature --	ISO 306/B50	100 °C
Vicat softening temperature	Vicat softening temperature	Vicat softening temperature --	ISO 306/A50	195 °C
Glass transition temperature	Glass transition temperature	ISO 11357-2	0.00 °C
Brittle temperature	Brittle temperature	ISO 974	-96.0 °C
Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed	ISO 75-2/A	45.0 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed	ISO 75-2/B	80.0 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD：--	ISO 11359-2	1.9E-04 cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD：-40to23°C	ISO 11359-2	1.6E-04 cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD：23to55°C	ASTME831	1.7E-04 cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD：--	ISO 11359-2	1.8E-04 cm/cm/°C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
density	density	ISO 1183	1.22 g/cm³
ThermalConductivityofMelt	ThermalConductivityofMelt		0.15 W/m/K
SpecificHeatCapacity of Melt	SpecificHeatCapacity of Melt		2150 J/kg/°C
melt mass-flow rate	melt mass-flow rate 230°C/2.16kg	ISO 1133	9.0 g/10min
MediumDensity	MediumDensity		1.06 g/cm³
Melt Volume Flow Rate (MVR)	Melt Volume Flow Rate (MVR) 230°C/2.16kg	ISO 1133	8.50 cm³/10min
Shrinkage rate	Shrinkage rate TD	ISO 294-4	1.5 %
Shrinkage rate	Shrinkage rate	Shrinkage rate MD	ISO 294-4	1.5 %
Water absorption rate	Water absorption rate 23°C,24hr	ISO 62	0.50 %
	Water absorption rate	Water absorption rate Saturation,23°C,2.00mm	ISO 62	0.60 %
	Water absorption rate	Water absorption rate	Water absorption rate Equilibrium,23°C,2.00mm,50%RH	ISO 62	0.20 %

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Dissipation factor	Dissipation factor 1MHz	IEC 60250	0.036
Dissipation factor	Dissipation factor	Dissipation factor 100Hz	IEC 60250	0.012
Relative permittivity	Relative permittivity 1MHz	IEC 60250	4.10
Surface resistivity	Surface resistivity	IEC 60093	>1.0E+15 ohms
Volume resistivity	Volume resistivity	IEC 60093	8E+13 ohms·cm
Dielectric strength	Dielectric strength	IEC 60243-1	20 kV/mm
Relative permittivity	Relative permittivity 100Hz	IEC 60250	4.60

hardness	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Shore hardness	Shore hardness ShoreD	ISO 868	63
Shore hardness	Shore hardness ShoreD,15Sec	ISO 868	57

hardness

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Shore hardness

ShoreD

ISO 868

Shore hardness

ShoreD,15Sec

ISO 868

Supplementary Information	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Odor	Odor	VDA270	2.50
EmissionofOrganicCompounds	EmissionofOrganicCompounds	VDA277	2.50 µgC/g

Supplementary Information

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Odor

VDA270

2.50

EmissionofOrganicCompounds

VDA277

2.50 µgC/g

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.