PA66 Alloy Orgalloy® RS 6600 ARKEMA FRANCE

So sánh

Bảng thông số kỹ thuật

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
tensile strength	tensile strength 50mm/min，Yield，23°C	ISO 527-2	51.5 MPa
Charpy Notched Impact Strength	Charpy Notched Impact Strength 简支梁Notched冲击强度	ISO 179/Af	12 kJ/m²
	Charpy Notched Impact Strength	Charpy Notched Impact Strength 弹性模量	ISO R527	2600 MPa
	Charpy Notched Impact Strength	Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C	ISO 179/1eA	17 kJ/m²
Bending modulus	Bending modulus 23°C	ISO 178	2300 MPa
Bending modulus	Bending modulus	Bending modulus 调节后50%RH和23°C	ISO 178	2100 MPa
bending strength	bending strength 23°C	ISO 178	75.0 MPa
bending strength	bending strength	bending strength 调节后50%RH和23°C	ISO 178	67.0 MPa
Tensile creep modulus	Tensile creep modulus 1000Hr	ISO 899-1	- MPa
Tensile creep modulus	Tensile creep modulus	Tensile creep modulus 1Hr	ISO 899-1	2270 MPa
Tensile modulus	Tensile modulus 1mm/min，23°C	ISO 527-2	- MPa
Elongation at Break	Elongation at Break 50mm/min，Yield，23°C	ISO 527-2	4.1 %
Elongation at Break	Elongation at Break	Elongation at Break 50mm/min，23°C	ISO 527-2	>=100 %
tensile strength	tensile strength 23°C	ISO 527-2	50.0 MPa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot deformation temperature	Hot deformation temperature 0.45MPaUnannealed	ISO 75-2/Bf	160 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD	ISO 11359-2	1.1E-04 cm/cm／°C
Hot deformation temperature	Hot deformation temperature 1.80MPaAnnealed	ISO 75-2/Af	80.0 °C
Vicat softening temperature	Vicat softening temperature 50N	ISO 306/A50	165 °C
	Vicat softening temperature	Vicat softening temperature 10N	ISO 306/B50	225 °C
	Vicat softening temperature	Vicat softening temperature	Vicat softening temperature Melting Temperature	ISO 11357-3	255 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD	ISO 11359-2	6.5E-05 cm/cm／°C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
melt mass-flow rate	melt mass-flow rate 吸水率	ISO 62	2.9 %
melt mass-flow rate	melt mass-flow rate	melt mass-flow rate 235℃/5.00Kg	ISO 1133	15 g/10min
Water absorption rate	Water absorption rate (23°C,50RH)	ISO 62	1.2 %
Water absorption rate	Water absorption rate	Water absorption rate (23°C,24hr)	ISO 62	0.70 %
density	density	ISO 1183	1.04 g/cm³

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Dissipation factor	Dissipation factor	IEC 60250	0.017
Dissipation factor	Dissipation factor	Dissipation factor	IEC 60250	0.025
Dielectric strength	Dielectric strength 1.00mm	IEC 60243-1	36.0 KV/mm
Surface resistivity	Surface resistivity	IEC 60093	2.5E+16 Ω.cm
Volume resistivity	Volume resistivity	IEC 60093	6E+15 Ω.cm
Dissipation factor	Dissipation factor	IEC 60250	0.032 1kHz
Dissipation factor	Dissipation factor	Dissipation factor 相对漏电起痕指数	IEC 60112	>=600 V

hardness	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hardness (Shore A)	Hardness (Shore A)	ISO 868	77

hardness

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Hardness (Shore A)

ISO 868

flame retardant performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
UL flame retardant rating	UL flame retardant rating	UL -94	HB -

flame retardant performance

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

UL flame retardant rating

UL -94

HB -

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.