PA+PPO(PPE) Infino HT-8200G LOTTE KOREA

So sánh

Bảng thông số kỹ thuật

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C	ISO 179/1eA	10 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C,3.18mm	ASTM D256	88 J/m
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C,6.35mm	ASTM D256	69 J/m
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ISO 180/1A	10 kJ/m²

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Tensile modulus	Tensile modulus	ASTM D638	8400 MPa
Tensile modulus	Tensile modulus	Tensile modulus	ISO 527-2/50	8800 MPa
tensile strength	tensile strength Yield	ASTM D638	140 MPa
Bending modulus	Bending modulus	ISO 178	11000 MPa
bending strength	bending strength	ASTM D790	240 MPa
bending strength	bending strength	bending strength	ISO 178	210 MPa
Bending modulus	Bending modulus	ASTM D790	5900 MPa
tensile strength	tensile strength Yield	ISO 527-2/50	159 MPa
	tensile strength	tensile strength Break	ASTM D638	140 MPa
	tensile strength	tensile strength	tensile strength Break	ISO 527-2/50	160 MPa
elongation	elongation Break	ASTM D638	3.0 %
Tensile strain	Tensile strain Break	ISO 527-2/50	3.0 %

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed,6.40mm	ASTM D648	250 °C
	Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed,4.00mm	ISO 75-2/B	254 °C
		Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed,6.40mm	ASTM D648	231 °C
		Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed,4.00mm	ISO 75-2/A	234 °C
Vicat softening temperature	Vicat softening temperature	ISO 306/B50	248 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Shrinkage rate	Shrinkage rate TD:3.20mm	ISO 2577	0.50to0.61 %
Shrinkage rate	Shrinkage rate	Shrinkage rate MD:3.20mm	ISO 2577	0.40to0.49 %
density	density	ASTM D792	1.24 g/cm³
density	density	density	ISO 1183	1.24 g/cm³
melt mass-flow rate	melt mass-flow rate 285°C/5.0kg	ASTM D1238	20 g/10min
melt mass-flow rate	melt mass-flow rate	melt mass-flow rate 285°C/5.0kg	ISO 1133	20 g/10min
Shrinkage rate	Shrinkage rate MD：3.20mm	ASTM D955	0.40to0.49 %
Shrinkage rate	Shrinkage rate	Shrinkage rate TD：3.20mm	ASTM D955	0.50to0.61 %

hardness	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Rockwell hardness	Rockwell hardness R-Scale	ASTM D785	117
Rockwell hardness	Rockwell hardness R-Scale	ISO 2039-2	117

hardness

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Rockwell hardness

R-Scale

ASTM D785

117

Rockwell hardness

R-Scale

ISO 2039-2

117

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.