PEEK VICTREX® 381G VICTREX UK

790

Giấy chứng nhận:
UL
So sánh
Xem giá

Bảng thông số kỹ thuật

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength 23°C	ISO 180	NoBreak
Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C	ISO 179/1eA	6.0 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch 23°C	ISO 179	NoBreak
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ISO 180/A	7.0 kJ/m²

flammability	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Burning wire flammability index	Burning wire flammability index 2.0mm	IEC 60695-2-12	960 °C
Extreme Oxygen Index	Extreme Oxygen Index --11	ISO 4589-2	24 %
Extreme Oxygen Index	Extreme Oxygen Index	Extreme Oxygen Index --12	ISO 4589-2	35 %
toxicity	toxicity COcontent	NES713	0.0740
	toxicity	toxicity CO2content	NES713	0.150
	toxicity	toxicity	toxicity Totalgases	NES713	0.220

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
tensile strength	tensile strength Yield,23°C	ISO 527-2	98.0 Mpa
Tensile modulus	Tensile modulus 23°C	ISO 527-2	4000 Mpa
Bending modulus	Bending modulus 23°C	ISO 178	3800 Mpa
Tensile strain	Tensile strain Break,23°C	ISO 527-2	45 %
bending strength	bending strength 3.5%Strain,23°C	ISO 178	125 Mpa
	bending strength	bending strength 23°C	ISO 178	165 Mpa
		bending strength	bending strength 125°C	ISO 178	85.0 Mpa
			bending strength	bending strength 175°C	ISO 178	19.0 Mpa
			bending strength	bending strength	bending strength 275°C	ISO 178	12.5 Mpa
Compressive stress	Compressive stress 23°C	ISO 604	125 Mpa
Compressive stress	Compressive stress	Compressive stress 120°C	ISO 604	70.0 Mpa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD：<143°C	ISO 11359-2	5.5E-05 cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD：>143°C	ISO 11359-2	1.2E-04 cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD：<143°C	ISO 11359-2	4.5E-05 cm/cm/°C
Melting temperature	Melting temperature	ISO 11357-3	343 °C
Glass transition temperature	Glass transition temperature --8	ISO 11357-2	150 °C
Glass transition temperature	Glass transition temperature	Glass transition temperature --7	ISO 11357-2	143 °C
Hot deformation temperature	Hot deformation temperature 1.8MPa,Annealed	ISO 75-2/A	160 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed	ISO 75-2/Af	152 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD：>143°C	ISO 11359-2	1.4E-04 cm/cm/°C
thermal conductivity	thermal conductivity 23°C9	ISO 22007-4	0.29 W/m/K
thermal conductivity	thermal conductivity	thermal conductivity 23°C10	ISO 22007-4	0.32 W/m/K
RTI Elec	RTI Elec	UL 746	260 °C
RTI Imp	RTI Imp	UL 746	180 °C
RTI Str	RTI Str	UL 746	240 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Water absorption rate	Water absorption rate 100°C，Saturation	ISO 62	0.55 %
Water absorption rate	Water absorption rate	Water absorption rate Saturation,23°C	ISO 62	0.45 %
Shrinkage rate	Shrinkage rate MD	ISO 294-4	1.0 %
Shrinkage rate	Shrinkage rate	Shrinkage rate TD	ISO 294-4	1.3 %
Spiral flow length	Spiral flow length	Internal Method	12.0 CM
density	density 比重	ISO 1183	1.30 g/cm³
MeltViscosity	MeltViscosity 400°C	ISO 11443	300 Pa·s

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Compared to the anti leakage trace index	Compared to the anti leakage trace index	IEC 60112	PLC 4
Dissipation factor	Dissipation factor 23°C,1MHz	IEC 60250	3E-03
Dielectric constant	Dielectric constant 200°C,50Hz	IEC 60250	4.50
Dielectric constant	Dielectric constant	Dielectric constant 23°C,50Hz	IEC 60250	3.20
Dielectric strength	Dielectric strength 2.00mm	IEC 60243-1	23 KV/mm
Volume resistivity	Volume resistivity 23°C	IEC 60093	1E+16 ohms·cm
	Volume resistivity	Volume resistivity 125°C	IEC 60093	1E+15 ohms·cm
	Volume resistivity	Volume resistivity	Volume resistivity 275°C	IEC 60093	1E+09 ohms·cm
Dielectric strength	Dielectric strength 0.0500mm	IEC 60243-1	190 KV/mm

hardness	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Shore hardness	Shore hardness ShoreD,23°C	ISO 868	85

hardness

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Shore hardness

ShoreD,23°C

ISO 868

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.