PPO NORYL™ V0150B-701 SABIC INNOVATIVE SHANGHAI

111

Đặc tính:
Chịu nhiệt độ cao
Dòng chảy cao
Gia cố sợi thủy tinh
Lĩnh vực ứng dụng:
Phụ tùng nội thất ô tô
Ứng dụng điện
So sánh
Xem giá

Bảng thông số kỹ thuật

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Charpy Notched Impact Strength	Charpy Notched Impact Strength -30°C	ISO 179/1eA	5.0 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C	ISO 179/1eA	14 kJ/m²
Dart impact	Dart impact 23°C, Total Energy	ASTM D3763	50.0 J

impact performance

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Charpy Notched Impact Strength

-30°C

ISO 179/1eA

5.0 kJ/m²

Charpy Notched Impact Strength

23°C

ISO 179/1eA

14 kJ/m²

Dart impact

23°C, Total Energy

ASTM D3763

50.0 J

flammability	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
UL flame retardant rating	UL flame retardant rating 1.5 mm	UL 94	V-0
UL flame retardant rating	UL flame retardant rating	UL flame retardant rating 2.0 mm	UL 94	5VA
Burning wire flammability index	Burning wire flammability index 1.0 mm	IEC 60695-2-12	960 °C
Hot filament ignition temperature	Hot filament ignition temperature 1.0 mm	IEC 60695-2-13	775 °C
	Hot filament ignition temperature	Hot filament ignition temperature 2.0 mm	IEC 60695-2-13	775 °C
	Hot filament ignition temperature	Hot filament ignition temperature	Hot filament ignition temperature 3.0 mm	IEC 60695-2-13	775 °C
Extreme Oxygen Index	Extreme Oxygen Index	ISO 4589-2	32 %

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Tensile modulus	Tensile modulus --3	ASTM D638	2500 Mpa
Tensile modulus	Tensile modulus	Tensile modulus --	ISO 527-2/1	2500 Mpa
tensile strength	tensile strength Yield4	ASTM D638	70.0 Mpa
	tensile strength	tensile strength Yield	ISO 527-2/50	70.0 Mpa
		tensile strength	tensile strength Break4	ASTM D638	60.0 Mpa
		tensile strength	tensile strength	tensile strength Break	ISO 527-2/50	55.0 Mpa
elongation	elongation Yield4	ASTM D638	5.0 %
	elongation	elongation Yield	ISO 527-2/50	4.0 %
		elongation	elongation Break4	ASTM D638	7.0 %
		elongation	elongation	elongation Break	ISO 527-2/50	10 %
Bending modulus	Bending modulus 50.0 mm Span5	ASTM D790	2550 Mpa
Bending modulus	Bending modulus	Bending modulus --6	ISO 178	2400 Mpa
bending strength	bending strength --6,7	ISO 178	110 Mpa
bending strength	bending strength	bending strength Yield, 50.0 mm Span5	ASTM D790	105 Mpa
Taber abraser	Taber abraser 1000 Cycles, 1000 g, CS-17 Wheel	Internal Method	35.0 mg

injection	Điều kiện kiểm tra	Kết quả kiểm tra
drying temperature	drying temperature	110 to 120 °C
drying time	drying time	2.0 to 3.0 hr
Hopper temperature	Hopper temperature	80 to 100 °C
Temperature at the rear of the barrel	Temperature at the rear of the barrel	260 to 280 °C
Temperature in the middle of the barrel	Temperature in the middle of the barrel	280 to 300 °C
Temperature at the front of the material cylinder	Temperature at the front of the material cylinder	300 to 320 °C
Spray nozzle temperature	Spray nozzle temperature	280 to 300 °C
Processing (melt) temperature	Processing (melt) temperature	300 to 320 °C
Mold temperature	Mold temperature	100 to 130 °C

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot deformation temperature	Hot deformation temperature 0.45 MPa, Unannealed, 4.00 mm, 100 mm Span10	ISO 75-2/Be	140 °C
	Hot deformation temperature	Hot deformation temperature 1.8 MPa, Unannealed, 3.20 mm	ASTM D648	135 °C
	Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.8 MPa, Unannealed, 4.00 mm, 100 mm Span10	ISO 75-2/Ae	130 °C
Vicat softening temperature	Vicat softening temperature --	ASTM D152511	155 °C
	Vicat softening temperature	Vicat softening temperature --	ISO 306/A50	160 °C
	Vicat softening temperature	Vicat softening temperature	Vicat softening temperature --	ISO 306/B50	145 °C
Ball Pressure Test	Ball Pressure Test 123 to 127°C	IEC 60695-10-2	通过
Ball Pressure Test	Ball Pressure Test	Ball Pressure Test 140°C12	IEC 60695-10-2	通过
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion Flow : -40 to 40°C	ASTM E831	7.5E-5 cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion Flow : 23 to 80°C	ISO 11359-2	7.0E-5 cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion Across Flow : -40 to 40°C	ASTM E831	7.5E-5 cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion Across Flow : 23 to 80°C	ISO 11359-2	9.0E-5 cm/cm/°C
thermal conductivity	thermal conductivity	ISO 8302	0.27 W/m/K
RTI Elec	RTI Elec	UL 746	110 °C
RTI Imp	RTI Imp	UL 746	105 °C
RTI	RTI	UL 746	115 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
melt mass-flow rate	melt mass-flow rate 280°C/5.0 kg	ASTM D1238	3.5 g/10 min
Melt Volume Flow Rate (MVR)	Melt Volume Flow Rate (MVR) 300°C/5.0 kg	ISO 1133	10.0 cm3/10min
Shrinkage rate	Shrinkage rate --2，Flow	Internal Method	0.50 - 0.70 %
Shrinkage rate	Shrinkage rate	Shrinkage rate 3.20 mm，Flow	Internal Method	0.50 - 0.70 %
Water absorption rate	Water absorption rate Saturation, 23°C	ISO 62	0.18 %
Water absorption rate	Water absorption rate	Water absorption rate Equilibrium, 23°C, 50% RH	ISO 62	0.060 %

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Surface resistivity	Surface resistivity	IEC 60093	> 1.0E+15 ohms
Volume resistivity	Volume resistivity	IEC 60093	1.0E+15 ohms·cm
Dielectric strength	Dielectric strength 0.800 mm, in Oil	IEC 60243-1	33 KV/mm
	Dielectric strength	Dielectric strength 1.60 mm, in Oil	IEC 60243-1	26 KV/mm
	Dielectric strength	Dielectric strength	Dielectric strength 3.20 mm, in Oil	IEC 60243-1	16 KV/mm
Relative permittivity	Relative permittivity 50 Hz	IEC 60250	2.80
	Relative permittivity	Relative permittivity 60 Hz	IEC 60250	2.80
	Relative permittivity	Relative permittivity	Relative permittivity 1 MHz	IEC 60250	2.70
Dissipation factor	Dissipation factor 50 Hz	IEC 60250	9.0E-4
	Dissipation factor	Dissipation factor 60 Hz	IEC 60250	9.0E-4
	Dissipation factor	Dissipation factor	Dissipation factor 1 MHz	IEC 60250	3.0E-3
Compared to the anti leakage trace index	Compared to the anti leakage trace index	IEC 60112	V

hardness	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Ball Pressure Test	Ball Pressure Test H 358/30	ISO 2039-1	113 Mpa

hardness

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Ball Pressure Test

H 358/30

ISO 2039-1

113 Mpa

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.

Có thể bạn cũng quan tâm

PPO V0150B-701 Nhựa đổi mới cơ sở (Thượng Hải)

$4,242/MT

PPO V0150B-701 Nhựa đổi mới cơ sở (Thượng Hải)

₫140.690/KG