mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Tensile yield stress (V=50mm/min)	Tensile yield stress (V=50mm/min) 干/湿		140/100 Mpa
Charpy Notched Impact Strength	Charpy Notched Impact Strength 30℃，干		60 KJ/m
Bending modulus	Bending modulus 干/湿		7100 Mpa
Fracture stress (V=50mm/min)	Fracture stress (V=50mm/min) 干/湿		140/100 Mpa
tensile strength	tensile strength	ASTM D638/ISO 527	140/100 kg/cm²(MPa)[Lb/in²]
Tensile modulus	Tensile modulus	ASTM D638/ISO 527	8500/6000 kg/cm²(MPa)[Lb/in²]
Elongation at Break	Elongation at Break	ASTM D638/ISO 527	3/4.5 %
Charpy Notched Impact Strength	Charpy Notched Impact Strength	ASTM D256/ISO 179	- kg·cm/cm(J/M)ft·lb/in
Charpy Notched Impact Strength	Charpy Notched Impact Strength	Charpy Notched Impact Strength	ASTM D256/ISO 179	13/17 kg·cm/cm(J/M)ft·lb/in
elongation	elongation ≤0.5%, +23℃，湿		3500 Mpa
Ball Pressure Test	Ball Pressure Test 干/湿		190 Mpa
Elongation at Break	Elongation at Break 干/湿，V=50mm/min		3/4.5 %
Charpy Notched Impact Strength	Charpy Notched Impact Strength +23℃，干/湿		13/17 KJ/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap +23℃，干/湿		11/17 KJ/m
Tensile modulus	Tensile modulus 干/湿		8500/6000 Mpa
Tensile creep modulus	Tensile creep modulus 1000h,湿		3500 Mpa
Elongation at Break	Elongation at Break 干/湿，V=50mm/min		3/4.5 %
impact strength	impact strength +23℃，干/湿		4/10 J
Charpy Notched Impact Strength	Charpy Notched Impact Strength +23℃，干/湿		65/70 KJ/m

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion （23-80）℃，Dry		2.5-3.5/6-8
Maximum operating temperature	Maximum operating temperature		220 °C
Hot deformation temperature	Hot deformation temperature 0.45MPa负荷，Dry		250 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	ASTM D696/ISO 11359	2.5-3.5/6-8 mm/mm.℃
Melting temperature	Melting temperature		260 ℃（℉）
Hot deformation temperature	Hot deformation temperature HDT	ASTM D648/ISO 75	250 1.8Mpa ℃（℉）
thermal conductivity	thermal conductivity Dry		0.27 W/(m.K)
Temperature index	Temperature index 在20000h/5000h，后拉伸强度下降50%时		139/157 °C
specific heat	specific heat Dry		1.5 J/(g.K)
Hot deformation temperature	Hot deformation temperature 1.8MPa负荷，Dry		250 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Water absorption rate	Water absorption rate	ASTM D570/ISO 62	5.7-6.3 %
density	density	ASTM D792/ISO 1183	1.34

Physical properties

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Water absorption rate

ASTM D570/ISO 62

5.7-6.3 %

density

ASTM D792/ISO 1183

1.34

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Loss angle	Loss angle 1MHz，干/湿		0.02/0.1
Surface resistivity	Surface resistivity 干/湿		>10 Ω
Volume resistivity	Volume resistivity 干/湿		10 Ω.cm
Dielectric strength	Dielectric strength K20/P50，干/湿		80/65 KV/mm
Compared to the Leakage Traceability Index (CTI)	Compared to the Leakage Traceability Index (CTI) 干/湿		CTI 500
Dielectric constant	Dielectric constant 1MHz，干/湿		3.7/5
Compared to the Leakage Traceability Index (CTI)	Compared to the Leakage Traceability Index (CTI) 干/湿		CTI 525 M
Volume resistivity	Volume resistivity	ASTM D257/IEC 60093	10^15/10^12 Ω.cm
Surface resistivity	Surface resistivity	ASTM D257/IEC 60093	10^13/10^10 Ω

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.