PA66 Vydyne® R533H BK10A0 Ascend Performance Materials Operations LLC
So sánhBảng thông số kỹ thuật
| impact performance | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Impact strength of simply supported beam without notch | Impact strength of simply supported beam without notch -30°C | ISO 179/1eU | 70 kJ/m² |
| Charpy Notched Impact Strength | Charpy Notched Impact Strength 23°C | ISO 179/1eA | 11 kJ/m² |
| Charpy Notched Impact Strength | Charpy Notched Impact Strength -30°C | ISO 179/1eA | 10 kJ/m² |
| Impact strength of cantilever beam gap | Impact strength of cantilever beam gap 23°C | ISO 180 | 12 kJ/m² |
| Impact strength of cantilever beam gap | Impact strength of cantilever beam gap -30°C | ISO 180 | 10 kJ/m² |
| Impact strength of simply supported beam without notch | Impact strength of simply supported beam without notch 23°C | ISO 179/1eU | 80 kJ/m² |
| flammability | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Hot filament ignition temperature | Hot filament ignition temperature 0.75mm | IEC 60695-2-13 | 750 °C |
| Burning wire flammability index | Burning wire flammability index 3.0mm | IEC 60695-2-12 | 875 °C |
| Burning wire flammability index | Burning wire flammability index 1.5mm | IEC 60695-2-12 | 700 °C |
| Hot filament ignition temperature | Hot filament ignition temperature 3.0mm | IEC 60695-2-13 | 750 °C |
| Hot filament ignition temperature | Hot filament ignition temperature 1.5mm | IEC 60695-2-13 | 725 °C |
| UL flame retardant rating | UL flame retardant rating 0.75mm | UL 94 | HB |
| UL flame retardant rating | UL flame retardant rating 1.5mm | UL 94 | HB |
| UL flame retardant rating | UL flame retardant rating 3.0mm | UL 94 | HB |
| Burning wire flammability index | Burning wire flammability index 0.75mm | IEC 60695-2-12 | 725 °C |
| mechanical properties | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Poisson's ratio | Poisson's ratio | ISO 527-2 | 0.40 |
| bending strength | bending strength 23°C | ISO 178 | 290 MPa |
| Bending modulus | Bending modulus 23°C | ISO 178 | 10200 MPa |
| Tensile strain | Tensile strain Break,23°C | ISO 527-2 | 3.0 % |
| tensile strength | tensile strength Break,23°C | ISO 527-2 | 205 MPa |
| Tensile modulus | Tensile modulus 23°C | ISO 527-2 | 10600 MPa |
| thermal performance | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| RTI Elec | RTI Elec 3.0mm | UL 746 | 140 °C |
| RTI Imp | RTI Imp 0.75mm | UL 746 | 125 °C |
| RTI Imp | RTI Imp 1.5mm | UL 746 | 125 °C |
| RTI Imp | RTI Imp 3.0mm | UL 746 | 125 °C |
| RTI Elec | RTI Elec 1.5mm | UL 746 | 140 °C |
| RTI Elec | RTI Elec 0.75mm | UL 746 | 140 °C |
| Linear coefficient of thermal expansion | Linear coefficient of thermal expansion TD：23to55°C,2.00mm | ISO 11359-2 | 1.1E-04 cm/cm/°C |
| Linear coefficient of thermal expansion | Linear coefficient of thermal expansion MD：23to55°C,2.00mm | ISO 11359-2 | 2.1E-05 cm/cm/°C |
| Melting temperature | Melting temperature | ISO 11357-3 | 260 °C |
| Hot deformation temperature | Hot deformation temperature 1.8MPa,Unannealed | ISO 75-2/A | 250 °C |
| Hot deformation temperature | Hot deformation temperature 0.45MPa,Unannealed | ISO 75-2/B | 260 °C |
| RTI Str | RTI Str 0.75mm | UL 746 | 140 °C |
| RTI Str | RTI Str 1.5mm | UL 746 | 140 °C |
| RTI Str | RTI Str 3.0mm | UL 746 | 140 °C |
| Physical properties | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Water absorption rate | Water absorption rate Equilibrium,23°C,50%RH | ISO 62 | 1.7 % |
| density | density | ISO 1183 | 1.40 g/cm³ |
| Shrinkage rate | Shrinkage rate TD:23°C,2.00mm | ISO 294-4 | 0.90 % |
| Shrinkage rate | Shrinkage rate MD:23°C,2.00mm | ISO 294-4 | 0.40 % |
| Water absorption rate | Water absorption rate 23°C,24hr | ISO 62 | 0.80 % |
| Electrical performance | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Hot wire ignition | Hot wire ignition 1.5mm | UL 746 | PLC 3 |
| Volume resistivity | Volume resistivity 0.750mm | IEC 60093 | 1E+13 ohms·cm |
| Dielectric strength | Dielectric strength 1.00mm | IEC 60243 | 20 kV/mm |
| Arc resistance | Arc resistance 3.00mm | ASTM D495 | PLC6 |
| Compared to the anti leakage trace index | Compared to the anti leakage trace index 3.00mm | IEC 60112 | PLC 2 |
| High arc combustion index | High arc combustion index 0.75mm | UL 746 | PLC 0 |
| High arc combustion index | High arc combustion index 1.5mm | UL 746 | PLC 0 |
| High arc combustion index | High arc combustion index 3.0mm | UL 746 | PLC 0 |
| High voltage arc tracing rate | High voltage arc tracing rate HVTR | UL 746 | PLC 1 |
| Hot wire ignition | Hot wire ignition 0.75mm | UL 746 | PLC 4 |
| Hot wire ignition | Hot wire ignition 3.0mm | UL 746 | PLC 4 |