ABS POLYLAC® PA-777D TAIWAN CHIMEI

362

Đặc tính:
Chịu nhiệt
Chống va đập trung bình
Lĩnh vực ứng dụng:
Bộ phận gia dụng
Lĩnh vực điện tử
Lĩnh vực điện
Lĩnh vực ô tô
Giấy chứng nhận:
MSDS
RoHS
UL
SGS
So sánh
Xem giá

Bảng thông số kỹ thuật

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ISO 180/1A	13 kJ/m²
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap -30°C	ISO 180/1A	7.0 kJ/m²
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C,6.40mm	ASTM D256	140 J/m
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C,3.20mm	ASTM D256	170 J/m
Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C	ISO 179	14 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	Charpy Notched Impact Strength -30°C	ISO 179	7.0 kJ/m²

flammability	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
UL flame retardant rating	UL flame retardant rating 1.5mm	UL 94	HB

flammability

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

UL flame retardant rating

1.5mm

UL 94

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
bending strength	bending strength --6	ISO 178	73.0 Mpa
bending strength	bending strength	bending strength --5	ASTM D790	66.5 Mpa
Bending modulus	Bending modulus --6	ISO 178	2300 Mpa
Bending modulus	Bending modulus	Bending modulus --5	ASTM D790	2210 Mpa
elongation	elongation Break	ISO 527-2/50	34 %
elongation	elongation	elongation Break4	ASTM D638	15 %
tensile strength	tensile strength Break	ISO 527-2/50	33.0 Mpa
	tensile strength	tensile strength Yield	ISO 527-2/50	45.0 Mpa
	tensile strength	tensile strength	tensile strength Yield4	ASTM D638	44.0 Mpa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed	ISO 75-2/A	97.0 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed	ASTM D648	105 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD	ISO 11359-2	8.5E-05 cm/cm/°C
Hot deformation temperature	Hot deformation temperature 1.8MPa,Annealed	ASTM D648	115 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.8MPa,Annealed	ISO 75-2/A	117 °C
Vicat softening temperature	Vicat softening temperature --	ASTM D15257	125 °C
	Vicat softening temperature	Vicat softening temperature --	ISO 306/A50	124 °C
	Vicat softening temperature	Vicat softening temperature	Vicat softening temperature --	ISO 306/B50	117 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Shrinkage rate	Shrinkage rate	ISO 294-4	0.30-0.60 %
Melt Volume Flow Rate (MVR)	Melt Volume Flow Rate (MVR) 220°C/10.0kg	ISO 1133	5.50 cm3/10min
melt mass-flow rate	melt mass-flow rate 220°C/10.0kg	ASTM D1238	5.5 g/10min
density	density 23°C	ISO 1183	1.06 g/cm³
density	density	density --3	ASTM D792	1.06 g/cm³

hardness	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Rockwell hardness	Rockwell hardness R-Scale	ASTM D785	115

hardness

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Rockwell hardness

R-Scale

ASTM D785

115

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.