Đặc tính:
Trong suốt
Lĩnh vực ứng dụng:
Hàng gia dụng
Bộ phận gia dụng
Lĩnh vực ô tô
Giấy chứng nhận:
UL
SGS
RoHS
MSDS
SGS
TDS
TDS
UL
MSDS
RoHS
SVHC
Processing
Statement
So sánh
Xem giá

Bảng thông số kỹ thuật

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ISO 180/1A	14 kJ/m²
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap -30°C	ISO 180/1A	7.0 kJ/m²
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C,6.40mm	ASTM D256	160 J/m
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C,3.20mm	ASTM D256	150 J/m
Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C	ISO 179	14 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	Charpy Notched Impact Strength -30°C	ISO 179	7.0 kJ/m²

flammability	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
UL flame retardant rating	UL flame retardant rating 1.5mm	UL 94	HB

flammability

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

UL flame retardant rating

1.5mm

UL 94

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
bending strength	bending strength --4	ASTM D790	53.9 Mpa
Bending modulus	Bending modulus --5	ISO 178	1900 Mpa
Bending modulus	Bending modulus	Bending modulus --4	ASTM D790	1900 Mpa
elongation	elongation Break	ISO 527-2/50	40 %
elongation	elongation	elongation Break3	ASTM D638	40 %
tensile strength	tensile strength --3	ASTM D638	39.7 Mpa
tensile strength	tensile strength	tensile strength Break	ISO 527-2/50	33.0 Mpa
bending strength	bending strength --5	ISO 178	57.0 Mpa
tensile strength	tensile strength Yield	ISO 527-2/50	42.0 Mpa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot deformation temperature	Hot deformation temperature 1.8MPa,Annealed	ISO 75-2/A	97.0 °C
Vicat softening temperature	Vicat softening temperature --	ASTM D15256	105 °C
	Vicat softening temperature	Vicat softening temperature --	ISO 306/A50	104 °C
	Vicat softening temperature	Vicat softening temperature	Vicat softening temperature --	ISO 306/B50	96.0 °C
Hot deformation temperature	Hot deformation temperature 1.8MPa,Annealed	ASTM D648	99.0 °C
	Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed	ISO 75-2/A	77.0 °C
	Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed	ASTM D648	88.0 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD	ISO 11359-2	9E-05 cm/cm/°C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
density	density 23°C	ISO 1183	1.08 g/cm³
density	density	density --	ASTM D792	1.08 g/cm³
Shrinkage rate	Shrinkage rate	ISO 294-4	0.30-0.70 %
melt mass-flow rate	melt mass-flow rate 200°C/5.0kg	ASTMD1238	3.0 g/10min

hardness	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Rockwell hardness	Rockwell hardness R-Scale	ASTM D785	107

hardness

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Rockwell hardness

R-Scale

ASTM D785

107

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.

Có thể bạn cũng quan tâm

ABS PA-758 Chimei Đài Loan

$2,546/MT

ABS PA-758 Chimei Đài Loan

₫71.460/KG

ABS PA-758 Chimei Đài Loan

₫71.575/KG