PEEK KT-850P USA Suwei

So sánh

Bảng thông số kỹ thuật

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	ASTM D256	不断裂
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	ASTM D256	69.4 J/m
bending strength	bending strength	ASTM D790	152 MPa
Bending modulus	Bending modulus	ASTM D790	3860 MPa
Elongation at Break	Elongation at Break	ASTM D638	20-30 %
elongation	elongation Yield	ASTM D638	5.2 %
tensile strength	tensile strength	ASTM D638	96.5 MPa
Tensile modulus	Tensile modulus	ASTM D638	3650 MPa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion -50~50℃	ASTM E831	0.000043 cm/cm/℃
Chain melting temperature	Chain melting temperature	ASTM D3417	340 ℃
Glass transition temperature	Glass transition temperature	ASTM D3417	150 ℃
Hot deformation temperature	Hot deformation temperature 1.82MPa，Unannealed	ASTM D648	162 ℃

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
melt mass-flow rate	melt mass-flow rate 2.16kg@400℃	ASTM D1238	10 g/10 min
density	density	ASTM D792	1.30
Water absorption rate	Water absorption rate 24hr	ASTM D570	0.10 %

Physical properties

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

melt mass-flow rate

2.16kg@400℃

ASTM D1238

10 g/10 min

density

ASTM D792

1.30

Water absorption rate

24hr

ASTM D570

0.10 %

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.