flammability	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Extreme Oxygen Index	Extreme Oxygen Index	ISO 4589-2	35 %
UL flame retardant rating	UL flame retardant rating 1.2mm	IEC 60695-11-10,-20	V-0
UL flame retardant rating	UL flame retardant rating	UL flame retardant rating 1.5mm	IEC 60695-11-10,-20	V-0
Burning wire flammability index	Burning wire flammability index 1.5mm	IEC 60695-2-12	960 °C
Burning wire flammability index	Burning wire flammability index	Burning wire flammability index 3.0mm	IEC 60695-2-12	960 °C
Hot filament ignition temperature	Hot filament ignition temperature 1.5mm	IEC 60695-2-13	850 °C
Hot filament ignition temperature	Hot filament ignition temperature	Hot filament ignition temperature 3.0mm	IEC 60695-2-13	875 °C

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Tensile modulus	Tensile modulus	ISO 527-2	6000 MPa
tensile strength	tensile strength Break	ISO 527-2	95.0 MPa
Tensile strain	Tensile strain Break	ISO 527-2	4.0 %
Bending modulus	Bending modulus	ISO 178	5500 MPa
bending strength	bending strength	ISO 178	145 MPa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD	ISO 11359-2	3E-05 cm/cm/°C
RTI Elec	RTI Elec 1.5mm	UL 746	130 °C
RTI Elec	RTI Elec	RTI Elec 3.0mm	UL 746	130 °C
RTI Imp	RTI Imp 1.5mm	UL 746	125 °C
RTI Imp	RTI Imp	RTI Imp 3.0mm	UL 746	130 °C
Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed	ISO 75-2/A	145 °C
Vicat softening temperature	Vicat softening temperature	ISO 306/B50	150 °C
Ball Pressure Test	Ball Pressure Test 125°C	IEC 60695-10-2	Pass
RTI Str	RTI Str 1.5mm	UL 746	125 °C
RTI Str	RTI Str	RTI Str 3.0mm	UL 746	130 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Water absorption rate	Water absorption rate Saturation,23°C	ISO 62	0.29 %
LimitingViscosity	LimitingViscosity	ISO 1628-4	56.0 cm³/g
ThermalConductivityofMelt	ThermalConductivityofMelt		0.29 W/m/K
density	density	ISO 1183	1.35 g/cm³
Melt Volume Flow Rate (MVR)	Melt Volume Flow Rate (MVR) 300°C/1.2kg	ISO 1133	3.00 cm³/10min
Shrinkage rate	Shrinkage rate TD	ISO 294-4	0.50 %
Shrinkage rate	Shrinkage rate	Shrinkage rate MD	ISO 294-4	0.20 %

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Dissipation factor	Dissipation factor 100Hz	IEC 60250	9E-04
Dissipation factor	Dissipation factor	Dissipation factor 1MHz	IEC 60250	9E-03
Compared to the anti leakage trace index	Compared to the anti leakage trace index CTI	UL 746	PLC 3
Compared to the anti leakage trace index	Compared to the anti leakage trace index	Compared to the anti leakage trace index	IEC 60112	PLC 3
Surface resistivity	Surface resistivity	IEC 60093	>1.0E+15 ohms
Volume resistivity	Volume resistivity	IEC 60093	>1.0E+15 ohms·cm
Dielectric strength	Dielectric strength	IEC 60243-1	29 kV/mm
Relative permittivity	Relative permittivity 100Hz	IEC 60250	3.25
Relative permittivity	Relative permittivity	Relative permittivity 1MHz	IEC 60250	3.20

hardness	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Rockwell hardness	Rockwell hardness M-Scale	ISO 2039-2	91

hardness

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Rockwell hardness

M-Scale

ISO 2039-2

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.