flammability	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
UL flame retardant rating	UL flame retardant rating 0.40mm	UL 94	V-2
Hot filament ignition temperature	Hot filament ignition temperature 3.0mm	IEC 60695-2-13	825 °C
Hot filament ignition temperature	Hot filament ignition temperature	Hot filament ignition temperature 1.0mm	IEC 60695-2-13	850 °C
UL flame retardant rating	UL flame retardant rating 1.0mm	UL 94	V-1
UL flame retardant rating	UL flame retardant rating	UL flame retardant rating 1.6mm	UL 94	V-0
Burning wire flammability index	Burning wire flammability index 1.0mm	IEC 60695-2-12	930 °C
Burning wire flammability index	Burning wire flammability index	Burning wire flammability index 3.0mm	IEC 60695-2-12	960 °C

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
bending strength	bending strength	ISO 178	142 Mpa
Bending modulus	Bending modulus	ISO 178	6500 Mpa
Tensile strain	Tensile strain Break	ISO 527-2/5	1.0 %
tensile strength	tensile strength Break	ISO 527-2/5	85.0 Mpa
Tensile modulus	Tensile modulus	ISO 527-2/1	6800 Mpa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
RTI	RTI 1.5mm	UL 746	80.0 °C
RTI Imp	RTI Imp 1.5mm	UL 746	80.0 °C
RTI Elec	RTI Elec 1.5mm	UL 746	80.0 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD	ISO 11359-2	6E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD	ISO 11359-2	3E-05 cm/cm/°C
Vicat softening temperature	Vicat softening temperature	ISO 306/B50	146 °C
Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed	ISO 75-2/A	140 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed	ISO 75-2/B	143 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Shrinkage rate	Shrinkage rate TD:4.00mm	Internal Method	0.30-0.50 %
Water absorption rate	Water absorption rate 23°C,24hr	ISO 62	0.12 %
Shrinkage rate	Shrinkage rate MD:4.00mm	Internal Method	0.10-0.30 %

Physical properties

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Shrinkage rate

TD:4.00mm

Internal Method

0.30-0.50 %

Water absorption rate

23°C,24hr

ISO 62

0.12 %

Shrinkage rate

MD:4.00mm

Internal Method

0.10-0.30 %

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Dissipation factor	Dissipation factor 100Hz	IEC 60250	1E-03
Dissipation factor	Dissipation factor	Dissipation factor 1MHz	IEC 60250	9E-03
Compared to the anti leakage trace index	Compared to the anti leakage trace index	IEC 60112	PLC 3
Dielectric constant	Dielectric constant 1MHz	IEC 60250	3.50
Dielectric constant	Dielectric constant	Dielectric constant 100Hz	IEC 60250	3.50
Dielectric strength	Dielectric strength	IEC 60243-1	35 KV/mm
Volume resistivity	Volume resistivity	IEC 60093	>1.0E+15 ohms·cm
Surface resistivity	Surface resistivity	IEC 60093	>1.0E+15 ohms

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.