PA6 9B23300 X 4Plas
So sánhBảng thông số kỹ thuật
| impact performance | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Impact strength of cantilever beam gap | Impact strength of cantilever beam gap -30°C | ISO 180/1A | 5.0 kJ/m² |
| Impact strength of cantilever beam gap | Impact strength of cantilever beam gap 23°C | ISO 180/1A | 6.0 kJ/m² |
| Suspended wall beam without notch impact strength | Suspended wall beam without notch impact strength -30°C | ISO 180/1U | 无断裂 |
| Suspended wall beam without notch impact strength | Suspended wall beam without notch impact strength 23°C | ISO 180/1U | 无断裂 |
| flammability | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| UL flame retardant rating | UL flame retardant rating 3.2mm | UL 94 | V-2 |
| UL flame retardant rating | UL flame retardant rating 3.20 mm | UL 94 | V-2 |
| mechanical properties | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Tensile modulus | Tensile modulus 23°C | ISO 527-2/5 | 3000 MPa |
| tensile strength | tensile strength Break,23°C | ISO 527-2/5 | 80.0 MPa |
| tensile strength | tensile strength Break, 23°C | ISO 527-2/5 | 80.0 MPa |
| Impact strength of cantilever beam gap | Impact strength of cantilever beam gap -30°C | ISO 180/1A | 5.0 kJ/m² |
| Impact strength of cantilever beam gap | Impact strength of cantilever beam gap 23°C | ISO 180/1A | 6.0 kJ/m² |
| Suspended wall beam without notch impact strength | Suspended wall beam without notch impact strength -30°C | ISO 180/1U | 无断裂 |
| Suspended wall beam without notch impact strength | Suspended wall beam without notch impact strength 23°C | ISO 180/1U | 无断裂 |
| Tensile modulus | Tensile modulus 23°C | ISO 527-2/5 | 3000 MPa |
| thermal performance | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Melting temperature | Melting temperature | ISO 11357 | 223 °C |
| Vicat softening temperature | Vicat softening temperature | ISO 306/B | 200 °C |
| Hot deformation temperature | Hot deformation temperature 0.45MPa,Unannealed | ISO 75-2/B | 180 °C |
| Hot deformation temperature | Hot deformation temperature 1.8MPa,Unannealed | ISO 75-2/A | 65.0 °C |
| Hot deformation temperature | Hot deformation temperature 0.45 MPa, Unannealed | ISO 75-2/B | 180 °C |
| Hot deformation temperature | Hot deformation temperature 1.8 MPa, Unannealed | ISO 75-2/A | 65.0 °C |
| Vicat softening temperature | Vicat softening temperature | ISO 306/B | 200 °C |
| Melting temperature | Melting temperature | ISO 11357 | 223 °C |
| Physical properties | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Shrinkage rate | Shrinkage rate TD | 1.2 % | |
| Shrinkage rate | Shrinkage rate MD | 1.2 % | |
| Water absorption rate | Water absorption rate Equilibrium,23°C,50%RH | ISO 62 | 3.0 % |
| density | density | ISO 1183 | 1.13 g/cm³ |
| density | density | ISO 1183 | 1.13 g/cm³ |
| Shrinkage rate | Shrinkage rate TD | ISO 1183 | 1.2 % |
| Shrinkage rate | Shrinkage rate MD | ISO 1183 | 1.2 % |
| Water absorption rate | Water absorption rate Equilibrium, 23°C, 50% RH | ISO 62 | 3.0 % |
| Electrical performance | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Surface resistivity | Surface resistivity | IEC 60093 | 1E+13 ohms |
| Volume resistivity | Volume resistivity | IEC 60093 | 1E+15 ohms·cm |
| Compared to the anti leakage trace index | Compared to the anti leakage trace index | IEC 60112 | PLC 0 |
| Surface resistivity | Surface resistivity | IEC 60093 | 1E+13 ohms |
| Volume resistivity | Volume resistivity | IEC 60093 | 1E+15 ohms·cm |
| Compared to the anti leakage trace index | Compared to the anti leakage trace index | IEC 60112 | PLC 0 |