flammability	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
UL flame retardant rating	UL flame retardant rating 0.43mm	UL 94	HB
UL flame retardant rating	UL flame retardant rating 0.8mm	UL 94	V-2
UL flame retardant rating	UL flame retardant rating 3.0mm	UL 94	V-1

flammability

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

UL flame retardant rating

0.43mm

UL 94

UL flame retardant rating

0.8mm

UL 94

V-2

UL flame retardant rating

3.0mm

UL 94

V-1

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Tensile modulus	Tensile modulus	ISO 527-2/1	6700 Mpa
tensile strength	tensile strength Break	ISO 527-2/5	100 Mpa
Tensile strain	Tensile strain Break	ISO 527-2/5	2.0 %
Bending modulus	Bending modulus	ISO 178	6600 Mpa
bending strength	bending strength	ISO 178	155 Mpa
Elongation at Break	Elongation at Break	ASTM D638/ISO 527	3.0 %
Tensile modulus	Tensile modulus	ASTM D638/ISO 527	6700 kg/cm²(MPa)[Lb/in²]
tensile strength	tensile strength	ASTM D638/ISO 527	108 kg/cm²(MPa)[Lb/in²]
Rockwell hardness	Rockwell hardness	ASTM D785	93
Bending modulus	Bending modulus	ASTM D790/ISO 178	6600 kg/cm²(MPa)[Lb/in²]
bending strength	bending strength	ASTM D790/ISO 178	155 kg/cm²(MPa)[Lb/in²]

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed	ISO 75-2/B	143 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed	ISO 75-2/A	139 °C
Vicat softening temperature	Vicat softening temperature	ISO 306/B50	146 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD	ISO 11359-2	3E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD	ISO 11359-2	6E-05 cm/cm/°C
RTI Elec	RTI Elec 1.5mm	UL 746	130 °C
RTI Imp	RTI Imp 1.5mm	UL 746	125 °C
RTI	RTI 1.5mm	UL 746	130 °C
Hot deformation temperature	Hot deformation temperature HDT	ASTM D648/ISO 75	146 ℃（℉）
Vicat softening temperature	Vicat softening temperature	ASTM D1525/ISO R306	146 ℃（℉）
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	ASTM D696/ISO 11359	0.000060 mm/mm.℃

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Shrinkage rate	Shrinkage rate TD:4.00mm	Internal Method	0.30-0.50 %
Shrinkage rate	Shrinkage rate	Shrinkage rate MD:4.00mm	Internal Method	0.10-0.30 %
Water absorption rate	Water absorption rate 23°C,24hr	ISO 62	0.12 %
Shrinkage rate	Shrinkage rate	ASTM D955	0.30-0.50 %
Water absorption rate	Water absorption rate	ASTM D570/ISO 62	0.12 %

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Surface resistivity	Surface resistivity	IEC 60093	>1.0E+15 ohms
Volume resistivity	Volume resistivity	IEC 60093	>1.0E+15 ohms·cm
Dielectric strength	Dielectric strength	IEC 60243-1	35 KV/mm
Relative permittivity	Relative permittivity 100Hz	IEC 60250	3.50
Relative permittivity	Relative permittivity	Relative permittivity 1MHz	IEC 60250	3.50
Dissipation factor	Dissipation factor 100Hz	IEC 60250	1E-03
Dissipation factor	Dissipation factor	Dissipation factor 1MHz	IEC 60250	9E-03
Compared to the anti leakage trace index	Compared to the anti leakage trace index	IEC 60112	PLC 3
Surface resistivity	Surface resistivity	ASTM D257/IEC 60093	1.0E+15 Ω
Dielectric constant	Dielectric constant	ASTM D150/IEC 60250	3.50
Volume resistivity	Volume resistivity	ASTM D257/IEC 60093	1.0E+15 Ω.cm
Dielectric loss	Dielectric loss	ASTM D150/IEC 60250	0.0010
Dielectric loss	Dielectric loss	Dielectric loss	ASTM D150/IEC 60250	0.0090

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.