ASA+PC UMG ALLOY® TA-15W UMG JAPAN

So sánh

Bảng thông số kỹ thuật

	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Tensile modulus	Tensile modulus 23°C	ISO 527-2	2300 MPa
Rockwell hardness	Rockwell hardness R-Sale,23°C	ISO 2039-2	113
Shrinkage rate	Shrinkage rate MD：23°C	ISO 294-4	0.50to0.70 %
Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C	ISO 179	45 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	Charpy Notched Impact Strength -30°C	ISO 179	7.0 kJ/m²
bending strength	bending strength 23°C	ISO 178	99.0 MPa
Bending modulus	Bending modulus 23°C	ISO 178	2750 MPa
tensile strength	tensile strength 23°C	ISO 527-2	59.0 MPa
Melt Volume Flow Rate (MVR)	Melt Volume Flow Rate (MVR) 220°C/10.0kg	ISO 1133	11.0 cm³/10min
density	density 23°C	ISO 1183	1.12 g/cm³
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD	ISO 11359-2	8E-05 cm/cm/°C
Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed	ISO 75-2/Af	97.0 °C

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.