PA66/PTFE LNP™ LUBRICOMP™ RFL-4038 SABIC INNOVATIVE US

311

Đặc tính:
Chống mài mòn
Ổn định nhiệt
Đóng gói: Gia cố sợi thủy
10% đóng gói theo trọng l
Lĩnh vực ứng dụng:
Túi nhựa
So sánh

Bảng thông số kỹ thuật

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Multi axis Instrumented Impact Energy	Multi axis Instrumented Impact Energy	ISO 6603-2	1.56 J
Dart impact	Dart impact 23°C,TotalEnergy	ASTM D3763	6.58 J
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength 23°C	ISO 180/1U	25 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ISO 180/1A	4.9 kJ/m²

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
bending strength	bending strength Break,50.0mmSpan	ASTM D790	165 Mpa
bending strength	bending strength	bending strength	ISO 178	159 Mpa
Bending modulus	Bending modulus	ISO 178	5020 Mpa
Bending modulus	Bending modulus	Bending modulus 50.0mmSpan	ASTM D790	5300 Mpa
Tensile strain	Tensile strain Break	ISO 527-2/5	2.7 %
elongation	elongation Break	ASTM D638	2.8 %
tensile strength	tensile strength Break	ISO 527-2/5	103 Mpa
tensile strength	tensile strength	tensile strength Break	ASTM D638	107 Mpa
Tensile modulus	Tensile modulus	ISO 527-2/1	5500 Mpa
Tensile modulus	Tensile modulus	Tensile modulus	ASTM D638	5640 Mpa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed,3.20mm	ASTM D648	246 °C
	Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed,64.0mmSpan	ISO 75-2/Bf	257 °C
	Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed,3.20mm	ASTM D648	260 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD：-30to30°C	ASTM D696	8.6E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD：-30to30°C	ASTM D696	4.7E-05 cm/cm/°C
Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed,64.0mmSpan	ISO 75-2/Af	240 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Water absorption rate	Water absorption rate 24hr,50%RH	ASTM D570	0.64 %
Shrinkage rate	Shrinkage rate TD：24hr	ASTM D955	1.0-3.0 %
Shrinkage rate	Shrinkage rate	Shrinkage rate MD：24hr	ASTM D955	0.50-0.70 %
Water absorption rate	Water absorption rate Equilibrium,23°C,50%RH	ISO 62	0.97 %

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.