ABS ABS H801 ELIX Polymers, S. L.

So sánh

Bảng thông số kỹ thuật

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ISO 180/1A	30 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength -30°C	ISO 179/1eA	12 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C	ISO 179/1eA	30 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap -30°C	ISO 180/1A	12 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch 23°C	ISO 179/1eU	220 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch -30°C	ISO 179/1eU	160 kJ/m²

flammability	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Burning rate	Burning rate 2.00mm	ISO 3795	45 mm/min
Burning wire flammability index	Burning wire flammability index 2.0mm	IEC 60695-2-12	700 °C

flammability

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Burning rate

2.00mm

ISO 3795

45 mm/min

Burning wire flammability index

2.0mm

IEC 60695-2-12

700 °C

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
bending strength	bending strength 23°C	ISO 178	77.0 MPa
Bending modulus	Bending modulus 23°C	ISO 178	2300 MPa
Tensile strain	Tensile strain Break,23°C	ISO 527-2/50	>15 %
Tensile strain	Tensile strain	Tensile strain Yield,23°C	ISO 527-2/50	3.0 %
tensile strength	tensile strength Yield,23°C	ISO 527-2/50	49.0 MPa
Tensile modulus	Tensile modulus 23°C	ISO 527-2/1	2400 MPa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Vicat softening temperature	Vicat softening temperature	ISO 306/B50	105 °C
Hot deformation temperature	Hot deformation temperature 1.8MPa,Annealed	ISO 75-2/A	99.0 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 0.45MPa,Annealed	ISO 75-2/B	106 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD：23to55°C	ISO 11359-2	8E-05 cm/cm/°C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Shrinkage rate	Shrinkage rate MD	ISO 294-4	0.50to0.70 %
Shrinkage rate	Shrinkage rate	Shrinkage rate TD	ISO 294-4	0.50to0.70 %
Melt Volume Flow Rate (MVR)	Melt Volume Flow Rate (MVR) 220°C/10.0kg	ISO 1133	9.00 cm³/10min
density	density	ISO 1183	1.07 g/cm³

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Compared to the anti leakage trace index	Compared to the anti leakage trace index SolutionA	IEC 60112	PLC 0
Dissipation factor	Dissipation factor 23°C,1MHz	IEC 60250	9E-03
Dissipation factor	Dissipation factor	Dissipation factor 23°C,100Hz	IEC 60250	5E-03
Relative permittivity	Relative permittivity 23°C,1MHz	IEC 60250	3.00
Relative permittivity	Relative permittivity	Relative permittivity 23°C,100Hz	IEC 60250	3.10
Surface resistivity	Surface resistivity	IEC 60093	1E+16 ohms
Volume resistivity	Volume resistivity	IEC 60093	1E+16 ohms·cm
Dielectric strength	Dielectric strength 23°C,1.00mm	IEC 60243-1	38 kV/mm

hardness	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Ball Pressure Test	Ball Pressure Test	ISO 2039-1	105 MPa

hardness

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Ball Pressure Test

ISO 2039-1

105 MPa

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.