PC+ABS T85 SG Covestro - Polycarbonates

So sánh

Bảng thông số kỹ thuật

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength 23°C	ISO 180	NoBreak
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength -30°C	ISO 180	NoBreak
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ISO 180/A	50 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap -30°C	ISO 180/A	40 kJ/m²
Multi axis Instrumented Impact Energy	Multi axis Instrumented Impact Energy 23°C	ISO 6603-2	46.0 J
Multi axis Instrumented Impact Energy	Multi axis Instrumented Impact Energy	Multi axis Instrumented Impact Energy -30°C	ISO 6603-2	52.0 J

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Tensile strain	Tensile strain Break,23°C	ISO 527-2/5	>50 %
Tensile strain	Tensile strain	Tensile strain Yield,23°C	ISO 527-2/50	4.9 %
tensile strength	tensile strength Break,23°C	ISO 527-2/5	54.0 MPa
tensile strength	tensile strength	tensile strength Yield,23°C	ISO 527-2/50	55.0 MPa
Tensile modulus	Tensile modulus 23°C	ISO 527-2/1	2300 MPa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Vicat softening temperature	Vicat softening temperature --	ISO 306/B50	129 °C
Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed	ISO 75-2/A	108 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD：23to55°C	ISO 11359-2	7E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD：23to55°C	ISO 11359-2	7.5E-05 cm/cm/°C
Vicat softening temperature	Vicat softening temperature --	ISO 306/B120	130 °C
Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed	ISO 75-2/B	128 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Water absorption rate	Water absorption rate Saturation,23°C	ISO 62	0.60 %
Shrinkage rate	Shrinkage rate MD:260°C,3.00mm	ISO 2577	0.55to0.75 %
Shrinkage rate	Shrinkage rate	Shrinkage rate TD:260°C,3.00mm	ISO 2577	0.55to0.75 %
Melt Volume Flow Rate (MVR)	Melt Volume Flow Rate (MVR) 260°C/5.0kg	ISO 1133	15.0 cm³/10min
density	density 23°C	ISO 1183	1.15 g/cm³
Water absorption rate	Water absorption rate Equilibrium,23°C,50%RH	ISO 62	0.20 %
MeltViscosity	MeltViscosity 260°C	ISO 11443-A	255 Pa·s

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Relative permittivity	Relative permittivity 23°C,1MHz	IEC 60250	2.90
Dissipation factor	Dissipation factor 23°C,100Hz	IEC 60250	2.5E-03
Relative permittivity	Relative permittivity 23°C,100Hz	IEC 60250	3.00
Volume resistivity	Volume resistivity 23°C	IEC 60093	1E+17 ohms·cm
Surface resistivity	Surface resistivity	IEC 60093	1E+17 ohms
Dielectric strength	Dielectric strength 23°C,1.00mm	IEC 60243-1	35 kV/mm
Dissipation factor	Dissipation factor 23°C,1MHz	IEC 60250	9E-03
Compared to the anti leakage trace index	Compared to the anti leakage trace index SolutionA	IEC 60112	PLC 3

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.