| thermosetting | thermosetting Elongationunderload,20N/cm2:200°C | IEC 60811-2-1 | 60 % |
| Change rate of tensile strength in air | Change rate of tensile strength in air 70°C,168hr,在IRM903油中 | | -10 % |
| Tensile strain | Tensile strain Break | IEC 60811-1-1 | 170 % |
| tensile strength | tensile strength | IEC 60811-1-1 | 10.0 MPa |
| melt mass-flow rate | melt mass-flow rate 190°C/21.6kg | Internal Method | 2.0 g/10min |
| density | density | BS2782620A | 1.48 g/cm³ |
| Tensile stress change rate | Tensile stress change rate 120°C,168hr，Break | IEC 60811-1-2 | -15 % |
| Tensile stress change rate | Tensile stress change rate 100°C,168hr,在IRM902油中，Break | | -2.8 % |
| Tensile stress change rate | Tensile stress change rate 100°C,72hr,在IRM902油中，Break | | 2.1 % |
| Tensile stress change rate | Tensile stress change rate 100°C,24hr,在IRM902油中，Break | | -13 % |
| Tensile stress change rate | Tensile stress change rate 70°C,168hr,在水中，Break | | -20 % |
| Tensile stress change rate | Tensile stress change rate 70°C,168hr,在IRM903油中，Break | | -17 % |
| Change rate of tensile strength in air | Change rate of tensile strength in air 120°C,168hr | IEC 60811-1-2 | 12 % |
| Change rate of tensile strength in air | Change rate of tensile strength in air 100°C,168hr,在IRM902油中 | | -6.0 % |
| Change rate of tensile strength in air | Change rate of tensile strength in air 100°C,72hr,在IRM902油中 | | 12 % |
| Change rate of tensile strength in air | Change rate of tensile strength in air 100°C,24hr,在IRM902油中 | | 7.7 % |
| Change rate of tensile strength in air | Change rate of tensile strength in air 70°C,168hr,在水中 | | -20 % |
| HalogenAcidGasEvolution | HalogenAcidGasEvolution | IEC 60754-1 | <0.50 % |
| Extreme Oxygen Index | Extreme Oxygen Index | ISO 4589-2 | 29 % |
| thermosetting | thermosetting Permanentelongationaftercooling | IEC 60811-2-1 | 5.0 % |