PC+Polyester XYLEX™ FXY330DF resin SABIC
So sánhBảng thông số kỹ thuật
| impact performance | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Impact strength of cantilever beam gap | Impact strength of cantilever beam gap -30°C9 | ISO 180/1A | 4.0 kJ/m² |
| Impact strength of cantilever beam gap | Impact strength of cantilever beam gap 23°C | ASTM D256 | 70 J/m |
| Impact strength of cantilever beam gap | Impact strength of cantilever beam gap 0°C | ASTM D256 | 64 J/m |
| Impact strength of cantilever beam gap | Impact strength of cantilever beam gap -30°C | ASTM D256 | 55 J/m |
| Charpy Notched Impact Strength | Charpy Notched Impact Strength 23°C | ISO 179/1eA | 7.0 kJ/m² |
| Impact strength of cantilever beam gap | Impact strength of cantilever beam gap 23°C9 | ISO 180/1A | 7.0 kJ/m² |
| Dart impact | Dart impact 23°C,TotalEnergy | ASTM D3763 | 60.0 J |
| mechanical properties | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| bending strength | bending strength --6,7 | ISO 178 | 77.0 MPa |
| Bending modulus | Bending modulus --6 | ISO 178 | 1600 MPa |
| Bending modulus | Bending modulus 50.0mmSpan5 | ASTM D790 | 1500 MPa |
| elongation | elongation Break | ISO 527-2/50 | >200 % |
| elongation | elongation Break4 | ASTM D638 | 170 % |
| elongation | elongation Yield | ISO 527-2/50 | >5.0 % |
| elongation | elongation Yield4 | ASTM D638 | 5.0 % |
| bending strength | bending strength Yield,50.0mmSpan5 | ASTM D790 | 67.0 MPa |
| tensile strength | tensile strength Yield4 | ASTM D638 | 47.0 MPa |
| Tensile modulus | Tensile modulus -- | ISO 527-2/1 | 1580 MPa |
| Tensile modulus | Tensile modulus --3 | ASTM D638 | 1440 MPa |
| tensile strength | tensile strength Yield | ISO 527-2/50 | 49.0 MPa |
| tensile strength | tensile strength Break4 | ASTM D638 | 49.0 MPa |
| tensile strength | tensile strength Break | ISO 527-2/50 | 50.0 MPa |
| thermal performance | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Hot deformation temperature | Hot deformation temperature 1.8MPa,Unannealed,64.0mmSpan10 | ISO 75-2/Af | 78.0 °C |
| Hot deformation temperature | Hot deformation temperature 1.8MPa,Unannealed,3.20mm | ASTM D648 | 72.0 °C |
| Linear coefficient of thermal expansion | Linear coefficient of thermal expansion TD:-40to40°C | ASTME831 | 9.4E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | Linear coefficient of thermal expansion MD:-40to40°C | ISO 11359-2 | 9E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | Linear coefficient of thermal expansion MD:-40to40°C | ASTME831 | 8.9E-05 cm/cm/°C |
| Vicat softening temperature | Vicat softening temperature -- | ISO 306/B120 | 93.0 °C |
| Vicat softening temperature | Vicat softening temperature -- | ISO 306/B50 | 92.0 °C |
| Vicat softening temperature | Vicat softening temperature -- | ASTM D152511 | 90.0 °C |
| Linear coefficient of thermal expansion | Linear coefficient of thermal expansion TD:-40to40°C | ISO 11359-2 | 9E-05 cm/cm/°C |
| Physical properties | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| density | density | ASTMD792 | 1.17 g/cm³ |
| melt mass-flow rate | melt mass-flow rate 265°C/2.16kg | ASTM D1238 | 15 g/10min |
| Melt Volume Flow Rate (MVR) | Melt Volume Flow Rate (MVR) 265°C/2.16kg | ISO 1133 | 13.0 cm³/10min |
| Water absorption rate | Water absorption rate Equilibrium,23°C,50%RH | ISO 62 | 0.27 % |
| Water absorption rate | Water absorption rate Saturation,23°C | ISO 62 | 0.70 % |
| Shrinkage rate | Shrinkage rate MD:3.20mm | Internal Method | 0.50to0.70 % |
| Shrinkage rate | Shrinkage rate TD:3.20mm | Internal Method | 0.40to0.60 % |