POM Delrin® 900P DUPONT USA

978

Đặc tính:
Chống mài mòn
Độ cứng cao
Sức mạnh cao
Tăng cường
Chống va đập cao
Dòng chảy cao
Lĩnh vực ứng dụng:
Lớp sợi
Sản phẩm tường mỏng
Giấy chứng nhận:
UL
UL
So sánh
Xem giá

Bảng thông số kỹ thuật

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ISO 180/1A	7.0 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap -40°C	ISO 180/1A	8.0 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch 23°C	ISO 179/1eU	200 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch -30°C	ISO 179/1eU	200 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C	ISO 179/1eA	8.0 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	Charpy Notched Impact Strength -30°C	ISO 179/1eA	7.0 kJ/m²

flammability	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Burning rate	Burning rate 1.00mm	ISO 3795	20 mm/min
Atomization	Atomization F-value(refraction)	ISO 6452	95 %
Atomization	Atomization	Atomization G-value(condensate)	ISO 6452	2E-04 g
UL flame retardant rating	UL flame retardant rating 1.5mm	IEC 60695-11-10,-20	HB
Extreme Oxygen Index	Extreme Oxygen Index	ISO 4589-2	23 %
FMVSS flammability	FMVSS flammability	FMVSS302	B
UL flame retardant rating	UL flame retardant rating 0.8mm	UL 94	HB
	UL flame retardant rating	UL flame retardant rating 1.5mm	UL 94	HB
	UL flame retardant rating	UL flame retardant rating	UL flame retardant rating 0.8mm	IEC 60695-11-10,-20	HB

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Friction coefficient	Friction coefficient vs.Itself-Dynamic,1hr	ASTM D1894	0.25
Bending modulus	Bending modulus	ISO 178	3000 Mpa
Tensile creep modulus	Tensile creep modulus 1000hr	ISO 899-1	1500 Mpa
Tensile creep modulus	Tensile creep modulus	Tensile creep modulus 1hr	ISO 899-1	2800 Mpa
Nominal tensile fracture strain	Nominal tensile fracture strain	ISO 527-2	23 %
Tensile modulus	Tensile modulus	ISO 527-2	3300 Mpa
tensile strength	tensile strength Yield	ISO 527-2	71.0 Mpa
Tensile strain	Tensile strain Yield	ISO 527-2	12 %

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Effective thermal diffusivity coefficient	Effective thermal diffusivity coefficient		8E-08 m²/s
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD	ISO 11359-2	1.2E-04 cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD	ISO 11359-2	1.2E-04 cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD：23to55°C	ASTME831	1E-04 cm/cm/°C
Melting temperature	Melting temperature	ISO 11357-3	178 °C
Vicat softening temperature	Vicat softening temperature	ISO 306/B50	160 °C
Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed	ISO 75-2/A	94.0 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed	ISO 75-2/B	162 °C
AnnealingTime-Optional	AnnealingTime-Optional		30.0 min/mm
AnnealingTemperature	AnnealingTemperature		160 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
density	density	ISO 1183	1.42 g/cm³
melt mass-flow rate	melt mass-flow rate	ISO 1133	25 g/10min
Melt Volume Flow Rate (MVR)	Melt Volume Flow Rate (MVR) 190°C/2.16kg	ISO 1133	21.0 cm3/10min
Shrinkage rate	Shrinkage rate TD	ISO 294-4	1.9 %
Shrinkage rate	Shrinkage rate	Shrinkage rate MD	ISO 294-4	1.9 %
Water absorption rate	Water absorption rate Saturation,23°C,2.00mm	ISO 62	1.4 %
Water absorption rate	Water absorption rate	Water absorption rate Equilibrium,23°C,2.00mm,50%RH	ISO 62	0.40 %

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Volume resistivity	Volume resistivity	IEC 60093	1E+14 ohms·cm
Relative permittivity	Relative permittivity 100Hz	IEC 60250	3.80
Surface resistivity	Surface resistivity	IEC 60093	>1.0E+15 ohms
Relative permittivity	Relative permittivity 1MHz	IEC 60250	3.80
Compared to the anti leakage trace index	Compared to the anti leakage trace index	IEC 60112	PLC 0
Hot wire ignition	Hot wire ignition 0.750mm	UL 746	PLC 4 sec

hardness	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Rockwell hardness	Rockwell hardness R-Sale	ISO 2039-2	120
Rockwell hardness	Rockwell hardness M-Sale	ISO 2039-2	92

hardness

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Rockwell hardness

R-Sale

ISO 2039-2

120

Rockwell hardness

M-Sale

ISO 2039-2

Supplementary Information	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
EmissionofOrganicCompounds	EmissionofOrganicCompounds	VDA277	4.30 µgC/g
Emission	Emission	VDA275	<8.00 mg/kg

Supplementary Information

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

EmissionofOrganicCompounds

VDA277

4.30 µgC/g

Emission

VDA275

<8.00 mg/kg

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.