impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength 23°C	ASTM D256	无断裂
Dart impact	Dart impact 23°C, 3.20 mm, Total Energy	ASTM D3763	87.0 J

impact performance

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Suspended wall beam without notch impact strength

23°C

ASTM D256

无断裂

Dart impact

23°C, 3.20 mm, Total Energy

ASTM D3763

87.0 J

flammability	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot filament ignition temperature	Hot filament ignition temperature 2.0 mm	IEC 60695-2-13	850 °C
Extreme Oxygen Index	Extreme Oxygen Index	ASTM D2863	26 %
Average degree of combustion	Average degree of combustion	ASTM D746	3 CM

flammability

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Hot filament ignition temperature

2.0 mm

IEC 60695-2-13

850 °C

Extreme Oxygen Index

ASTM D2863

26 %

Average degree of combustion

ASTM D746

3 CM

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Tensile modulus	Tensile modulus	ASTM D638	2410 Mpa
tensile strength	tensile strength Yield, 23°C2	ASTM D638	60.0 Mpa
tensile strength	tensile strength	tensile strength Break	ASTM D638	71.0 Mpa
elongation	elongation Yield	ASTM D638	6.0 %
elongation	elongation	elongation Break	ASTM D638	150 %
Bending modulus	Bending modulus	ASTM D790	2410 Mpa
bending strength	bending strength	ASTM D790	96.0 Mpa
Wear resistance - Change in Haze	Wear resistance - Change in Haze	ASTM D1004	45 %

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot deformation temperature	Hot deformation temperature 0.45 MPa, Annealed, 4.00 mm	ASTM D648	144 °C
	Hot deformation temperature	Hot deformation temperature 1.8 MPa, Unannealed, 4.00 mm	ASTM D648	128 °C
	Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.8 MPa, Annealed, 4.00 mm	ASTM D648	141 °C
Vicat softening temperature	Vicat softening temperature	ASTM D15256	149 °C
Ball pressure temperature	Ball pressure temperature	IEC 60598-1	> 125 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion -40 to 82°C，Flow	ASTM D696	6.8E-5 cm/cm/°C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
melt mass-flow rate	melt mass-flow rate 300°C/1.2 kg	ASTM D1238	10 g/10 min
Shrinkage rate	Shrinkage rate Flow	ASTM D955	0.50 - 0.70 %
Water absorption rate	Water absorption rate 24 hr, 23°C	ASTM D570	0.15 %
Water absorption rate	Water absorption rate	Water absorption rate Equilibrium, 23°C, 50% RH	ASTM D570	0.32 %

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Volume resistivity	Volume resistivity 23°C	ASTM D257	2.0E+17 ohms·cm
Dielectric strength	Dielectric strength	ASTM D149	17 KV/mm
Dielectric constant	Dielectric constant 60 Hz	ASTM D150	3.00
Dissipation factor	Dissipation factor 60 Hz	ASTM D150	1.0E-3
Compared to the anti leakage trace index	Compared to the anti leakage trace index 2.00 mm	IEC 60112	PLC 2

hardness	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Rockwell hardness	Rockwell hardness M-Scale	ASTM D785	73
Rockwell hardness	Rockwell hardness R-Scale	ASTM D785	118

hardness

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Rockwell hardness

M-Scale

ASTM D785

Rockwell hardness

R-Scale

ASTM D785

118

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.