PPO(PPE)+PS+PA NORYL GTX™ GTX979 resin SABIC

So sánh

Bảng thông số kỹ thuật

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Charpy Notched Impact Strength	Charpy Notched Impact Strength -30°C	ISO 179/1eA	12 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C	ISO 179/1eA	20 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap -30°C	ASTM D256	150 J/m
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ASTM D256	220 J/m
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap -30°C9	ISO 180/1A	7.0 kJ/m²
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C9	ISO 180/1A	17 kJ/m²
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength -30°C	ISO 180/1U	无断裂
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength 23°C	ISO 180/1U	无断裂
Dart impact	Dart impact 23°C,TotalEnergy	ASTM D3763	50.0 J

flammability	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Burning wire flammability index	Burning wire flammability index 3.2mm	IEC 60695-2-12	650 °C

flammability

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Burning wire flammability index

3.2mm

IEC 60695-2-12

650 °C

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
tensile strength	tensile strength Break4	ASTM D638	50.0 MPa
bending strength	bending strength Yield,50.0mmSpan5	ASTM D790	80.0 MPa
bending strength	bending strength	bending strength --6,7	ISO 178	80.0 MPa
Bending modulus	Bending modulus --6	ISO 178	2150 MPa
Bending modulus	Bending modulus	Bending modulus 50.0mmSpan5	ASTM D790	2050 MPa
elongation	elongation Break	ISO 527-2/50	30 %
	elongation	elongation Break4	ASTM D638	60 %
		elongation	elongation Yield	ISO 527-2/50	4.0 %
		elongation	elongation	elongation Yield4	ASTM D638	5.0 %
tensile strength	tensile strength Break	ISO 527-2/50	50.0 MPa
	tensile strength	tensile strength Yield	ISO 527-2/50	55.0 MPa
	tensile strength	tensile strength	tensile strength Yield4	ASTM D638	55.0 MPa
Tensile modulus	Tensile modulus --	ISO 527-2/1	2100 MPa
Tensile modulus	Tensile modulus	Tensile modulus --3	ASTM D638	2000 MPa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD:-40to40°C	ASTME831	9.5E-05 cm/cm/°C
Vicat softening temperature	Vicat softening temperature --	ISO 306/B120	182 °C
Vicat softening temperature	Vicat softening temperature	Vicat softening temperature --	ASTMD152511	180 °C
Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed,100mmSpan10	ISO 75-2/Be	178 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed,3.20mm	ASTM D648	185 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD:23to80°C	ISO 11359-2	9.6E-05 cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD:-40to40°C	ASTME831	1E-04 cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD:23to80°C	ISO 11359-2	9.6E-05 cm/cm/°C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
density	density	ASTMD792	1.08 g/cm³
Water absorption rate	Water absorption rate Equilibrium,23°C,50%RH	ISO 62	1.2 %
Water absorption rate	Water absorption rate	Water absorption rate Saturation,23°C	ISO 62	4.2 %
melt mass-flow rate	melt mass-flow rate 280°C/5.0kg	ASTM D1238	15 g/10min
Melt Volume Flow Rate (MVR)	Melt Volume Flow Rate (MVR) 280°C/5.0kg	ISO 1133	11.0 cm³/10min
Shrinkage rate	Shrinkage rate MD:3.20mm	Internal Method	1.2to1.6 %
Shrinkage rate	Shrinkage rate	Shrinkage rate TD:3.20mm	Internal Method	1.2to1.6 %

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Volume resistivity	Volume resistivity	Internal Method	1.0E+3到1.0E+4 ohms·cm

Electrical performance

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Volume resistivity

Internal Method

1.0E+3到1.0E+4 ohms·cm

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.