PP TechnoFiber PP LGF 50-10-01 HI TECHNOCOMPOUND GERMANY

So sánh

Bảng thông số kỹ thuật

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C	ISO 179/1eA	23 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	Charpy Notched Impact Strength -30°C	ISO 179/1eA	22 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch 23°C	ISO 179/1eU	60 kJ/m²
	Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch -30°C	ISO 179/1eU	60 kJ/m²
		Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch 23°C	ISO 179/1eU	60 kJ/m²
		Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch -30°C	ISO 179/1eU	60 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C	ISO 179/1eA	23 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	Charpy Notched Impact Strength -30°C	ISO 179/1eA	22 kJ/m²

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
bending strength	bending strength	ISO 178	140 MPa
Bending modulus	Bending modulus	ISO 178	11200 MPa
tensile strength	tensile strength Yield	ISO 527-2/50	125 MPa
Tensile strain	Tensile strain Yield	ISO 527-2/50	2.1 %
Tensile modulus	Tensile modulus	ISO 527-2/1	11200 MPa
Tensile modulus	Tensile modulus	Tensile modulus	ISO 527-2/1	11200 MPa
bending strength	bending strength	ISO 178	140 MPa
Bending modulus	Bending modulus	ISO 178	11200 MPa
Tensile strain	Tensile strain Yield	ISO 527-2/50	2.1 %
tensile strength	tensile strength Yield	ISO 527-2/50	125 MPa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed	ISO 75-2/A	151 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 8.0MPa,Unannealed	ISO 75-2/C	130 °C
Melting temperature	Melting temperature	ISO 11357-3	165 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD:23to80°C	ISO 11359-2	1.3E-05 cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD:23to80°C	ISO 11359-2	1.7E-05 cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD:23to80°C	ISO 11359-2	1.3E-05 cm/cm/°C
Melting temperature	Melting temperature	ISO 11357-3	165 °C
Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed	ISO 75-2/B	160 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD:23to80°C	ISO 11359-2	1.7E-05 cm/cm/°C
Hot deformation temperature	Hot deformation temperature 8.0MPa,Unannealed	ISO 75-2/C	130 °C
	Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed	ISO 75-2/A	151 °C
	Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed	ISO 75-2/B	160 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Shrinkage rate	Shrinkage rate MD2	ISO 294-4	0.20 %
density	density	ISO 1183	1.31 g/cm³
density	density	density	ISO 1183	1.31 g/cm³
Shrinkage rate	Shrinkage rate MD2	ISO 294-4	0.20 %

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.