| Relative permittivity | Relative permittivity 1MHz | IEC 60250 | 2.90 |
| Dissipation factor | Dissipation factor 1MHz | IEC 60250 | 0.015 |
| Water absorption rate | Water absorption rate Equilibrium,23°C,50%RH | ISO 62 | 1.8 % |
| density | density 23°C | ISO 1183 | 1.07 g/cm³ |
| Melt Volume Flow Rate (MVR) | Melt Volume Flow Rate (MVR) 220°C/10.0kg | ISO 1133 | 30.0 cm³/10min |
| Water absorption rate | Water absorption rate Saturation,23°C | ISO 62 | 6.1 % |
| Vicat softening temperature | Vicat softening temperature | ISO 306/B50 | 140 °C |
| Volume resistivity | Volume resistivity | IEC 60093 | 1E+13 ohms·cm |
| Tensile modulus | Tensile modulus 23°C | ISO 527-2/1 | 1900 MPa |
| tensile strength | tensile strength Yield,23°C | ISO 527-2/50 | 45.0 MPa |
| Tensile strain | Tensile strain Yield,23°C | ISO 527-2/50 | 3.8 % |
| Charpy Notched Impact Strength | Charpy Notched Impact Strength 23°C | ISO 179/1eA | 14 kJ/m² |
| Impact strength of simply supported beam without notch | Impact strength of simply supported beam without notch 23°C | ISO 179/1eU | 无断裂 |
| Hot deformation temperature | Hot deformation temperature 0.45MPa,Unannealed | ISO 75-2/B | 115 °C |