PC+PET Makroblend® DP7645 Covestro - Polycarbonates
So sánhBảng thông số kỹ thuật
| impact performance | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Impact strength of simply supported beam without notch | Impact strength of simply supported beam without notch -30°C | ISO 179/1eU | NoBreak |
| Impact strength of simply supported beam without notch | Impact strength of simply supported beam without notch 23°C | ISO 179/1eU | NoBreak |
| Impact strength of cantilever beam gap | Impact strength of cantilever beam gap -20°C | ISO 180/A | 23 kJ/m² |
| Impact strength of cantilever beam gap | Impact strength of cantilever beam gap -10°C | ISO 180/A | 45 kJ/m² |
| Impact strength of cantilever beam gap | Impact strength of cantilever beam gap 23°C | ISO 180/A | 50 kJ/m² |
| Suspended wall beam without notch impact strength | Suspended wall beam without notch impact strength -30°C | ISO 180 | NoBreak |
| Suspended wall beam without notch impact strength | Suspended wall beam without notch impact strength 23°C | ISO 180 | NoBreak |
| Charpy Notched Impact Strength | Charpy Notched Impact Strength 23°C | ISO 179/1eA | 55 kJ/m² |
| flammability | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| UL flame retardant rating | UL flame retardant rating 0.8mm | UL 94 | HB |
| UL flame retardant rating | UL flame retardant rating 1.6mm | UL 94 | HB |
| Extreme Oxygen Index | Extreme Oxygen Index | ISO 4589-2 | 20 % |
| Burning rate - US-FMVSS | Burning rate - US-FMVSS >1.00mm | ISO 3795 | passed |
| mechanical properties | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Tensile modulus | Tensile modulus 23°C | ISO 527-2/1 | 2100 MPa |
| tensile strength | tensile strength Yield,23°C | ISO 527-2/50 | 50.0 MPa |
| tensile strength | tensile strength Break,23°C | ISO 527-2/50 | 40.0 MPa |
| Tensile strain | Tensile strain Yield,23°C | ISO 527-2/50 | 4.5 % |
| Nominal tensile fracture strain | Nominal tensile fracture strain 23°C | ISO 527-2/50 | >50 % |
| Bending modulus | Bending modulus 23°C | ISO 178 | 2100 MPa |
| bending strength | bending strength 23°C | ISO 178 | 75.0 MPa |
| bending strength | bending strength 3.5%Strain,23°C | ISO 178 | 65.0 MPa |
| Bending strain | Bending strain 23°C | ISO 178 | 5.7 % |
| thermal performance | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Hot deformation temperature | Hot deformation temperature 1.8MPa,Unannealed | ISO 75-2/A | 94.0 °C |
| Vicat softening temperature | Vicat softening temperature | ISO 306/B120 | 133 °C |
| Linear coefficient of thermal expansion | Linear coefficient of thermal expansion MD：23to55°C | ISO 11359-2 | 7E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | Linear coefficient of thermal expansion TD：23to55°C | ISO 11359-2 | 7E-05 cm/cm/°C |
| thermal conductivity | thermal conductivity 23°C | ISO 8302 | 0.20 W/m/K |
| Physical properties | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Apparent density | Apparent density | ISO 60 | 0.70 g/cm³ |
| Melt Volume Flow Rate (MVR) | Melt Volume Flow Rate (MVR) 260°C/5.0kg | ISO 1133 | 12.0 cm³/10min |
| Shrinkage rate | Shrinkage rate TD2 | ISO 2577 | 0.60to0.80 % |
| Shrinkage rate | Shrinkage rate TD:90°C,1hr | ISO 2577 | 0.10to0.20 % |
| Shrinkage rate | Shrinkage rate MD2 | ISO 2577 | 0.60to0.80 % |
| Shrinkage rate | Shrinkage rate MD:90°C,1hr | ISO 2577 | 0.10to0.20 % |
| density | density 23°C | ISO 1183 | 1.20 g/cm³ |
| hardness | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Ball Pressure Test | Ball Pressure Test | ISO 2039-1 | 100 MPa |
| Supplementary Information | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| GottfertMeltViscosity | GottfertMeltViscosity 260°C | Internal Method | 600 Pa·s |