impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch 23°C	ISO 179/1eU	52 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch -30°C	ISO 179/1eU	43 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength -30°C	ISO 179/1eA	6.0 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C	ISO 179/1eA	7.0 kJ/m²

flammability	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
UL flame retardant rating	UL flame retardant rating 0.8mm	UL 94	HB
Burning rate	Burning rate 1.00mm	FMVSS302	<100 mm/min
Burning wire flammability index	Burning wire flammability index 1.6mm	IEC 60695-2-12	650 °C

flammability

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

UL flame retardant rating

0.8mm

UL 94

Burning rate

1.00mm

FMVSS302

<100 mm/min

Burning wire flammability index

1.6mm

IEC 60695-2-12

650 °C

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
bending strength	bending strength	ISO 178	180 MPa
Bending modulus	Bending modulus	ISO 178	5200 MPa
Tensile strain	Tensile strain Break	ISO 527-2/5	3.0 %
tensile strength	tensile strength Break	ISO 527-2/5	120 MPa
Tensile modulus	Tensile modulus	ISO 527-2/1	6100 MPa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
TemperatureIndex	TemperatureIndex 50%LossofTensileStrength,5000hr	IEC 216	160to175 °C
Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed	ISO 75-2/B	220 °C
Melting temperature	Melting temperature	DIN EN11357-1	220 °C
Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed	ISO 75-2/A	205 °C
TemperatureIndex	TemperatureIndex 50%LossofTensileStrength,20000hr	IEC 216	130to150 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Water absorption rate	Water absorption rate 70°C	ISO 1110	2.6to2.9 %
Water absorption rate	Water absorption rate	Water absorption rate Saturation,23°C	ISO 62	7.7to8.3 %
density	density 23°C	ISO 1183	1.23 g/cm³
Shrinkage rate	Shrinkage rate MD	ISO 294-4	0.30 %
Shrinkage rate	Shrinkage rate	Shrinkage rate TD	ISO 294-4	0.70 %
Spiral flow length	Spiral flow length	Internal Method	87.0 cm

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Compared to the anti leakage trace index	Compared to the anti leakage trace index SolutionA	IEC 60112	PLC 0
Volume resistivity	Volume resistivity	IEC 60093	1E+13 ohms·cm
Surface resistivity	Surface resistivity	IEC 60093	1E+12 ohms

Electrical performance

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Compared to the anti leakage trace index

SolutionA

IEC 60112

PLC 0

Volume resistivity

IEC 60093

1E+13 ohms·cm

Surface resistivity

IEC 60093

1E+12 ohms

hardness	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Ball Pressure Test	Ball Pressure Test H961/30	ISO 2039-1	180 MPa

hardness

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Ball Pressure Test

H961/30

ISO 2039-1

180 MPa

Supplementary Information	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
ReinforcementContent	ReinforcementContent	ISO 1172	15 %

Supplementary Information

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

ReinforcementContent

ISO 1172

15 %

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.