mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
bending strength	bending strength 23℃	ASTM D-790	59 Mpa
Bending modulus	Bending modulus 23℃	ASTM D-790	2250 Mpa
Elongation at Break	Elongation at Break 23℃	ASTM D-638	20 %
tensile strength	tensile strength 23℃	ASTM D-638	44 Mpa
Rockwell hardness	Rockwell hardness 23℃	ASTM D-785	113 R-Scale
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap -30℃,6.4mmt	ASTM D-256	118 J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23℃ 6.4mmt	ASTM D-256	294 J/m

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
UL flame retardant rating	UL flame retardant rating	UL 94	HB calss
Vicat softening temperature	Vicat softening temperature 1.0kgf	ASTM D-1525	107 °C
Hot deformation temperature	Hot deformation temperature 1.82Mpa	ASTM D-648	88 °C

thermal performance

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

UL flame retardant rating

UL 94

HB calss

Vicat softening temperature

1.0kgf

ASTM D-1525

107 °C

Hot deformation temperature

1.82Mpa

ASTM D-648

88 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Shrinkage rate	Shrinkage rate	ASTM D-955	0.4-0.6 %

Physical properties

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Shrinkage rate

ASTM D-955

0.4-0.6 %

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.