PP SABIC® PPcompound 19T1020 SABIC
So sánhBảng thông số kỹ thuật
| impact performance | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Impact strength of cantilever beam gap | Impact strength of cantilever beam gap 23°C,3.20mm | ASTM D256 | 22 J/m |
| Impact strength of cantilever beam gap | Impact strength of cantilever beam gap -30°C | ISO 180/1A | 1.3 kJ/m² |
| Impact strength of cantilever beam gap | Impact strength of cantilever beam gap 23°C | ISO 180/1A | 2.5 kJ/m² |
| Suspended wall beam without notch impact strength | Suspended wall beam without notch impact strength 23°C,3.20mm | ASTM D4812 | 410 J/m |
| Impact strength of cantilever beam gap | Impact strength of cantilever beam gap -30°C | ISO 180/1A | 1.3 kJ/m² |
| Impact strength of cantilever beam gap | Impact strength of cantilever beam gap 23°C | ISO 180/1A | 2.5 kJ/m² |
| Suspended wall beam without notch impact strength | Suspended wall beam without notch impact strength 23°C,3.20mm | ASTM D4812 | 410 J/m |
| Charpy Notched Impact Strength | Charpy Notched Impact Strength -30°C6 | ISO 179/1eA | 1.1 kJ/m² |
| Charpy Notched Impact Strength | Charpy Notched Impact Strength 23°C7 | ISO 179/1eA | 2.5 kJ/m² |
| Impact strength of cantilever beam gap | Impact strength of cantilever beam gap 23°C,3.20mm | ASTM D256 | 22 J/m |
| InstrumentedDartImpact | InstrumentedDartImpact 23°C,EnergyatPeakLoad | ASTM D3763 | 3.30 J |
| Charpy Notched Impact Strength | Charpy Notched Impact Strength -30°C6 | ISO 179/1eA | 1.1 kJ/m² |
| Charpy Notched Impact Strength | Charpy Notched Impact Strength 23°C7 | ISO 179/1eA | 2.5 kJ/m² |
| InstrumentedDartImpact | InstrumentedDartImpact 23°C,EnergyatPeakLoad | ASTM D3763 | 3.30 J |
| mechanical properties | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Tensile modulus | Tensile modulus | ISO 527-2/1 | 3210 MPa |
| tensile strength | tensile strength Yield | ASTM D638 | 36.0 MPa |
| tensile strength | tensile strength Yield | ISO 527-2/50 | 36.0 MPa |
| tensile strength | tensile strength Break | ASTM D638 | 29.0 MPa |
| tensile strength | tensile strength Break | ISO 527-2/1A/50 | 32.7 MPa |
| elongation | elongation Yield | ASTM D638 | 5.0 % |
| Tensile strain | Tensile strain Yield | ISO 527-2/50 | 4.5 % |
| elongation | elongation Break | ASTM D638 | 21 % |
| Tensile strain | Tensile strain Break | ISO 527-2/50 | 11 % |
| Bending modulus | Bending modulus 50.0mmSpan4 | ASTM D790 | 2500 MPa |
| Bending modulus | Bending modulus 50.0mmSpan5 | ISO 178 | 3180 MPa |
| Tensile modulus | Tensile modulus | ASTM D638 | 2970 MPa |
| Tensile modulus | Tensile modulus | ISO 527-2/1 | 3210 MPa |
| tensile strength | tensile strength Yield | ASTM D638 | 36.0 MPa |
| tensile strength | tensile strength Yield | ISO 527-2/50 | 36.0 MPa |
| tensile strength | tensile strength Break | ASTM D638 | 29.0 MPa |
| tensile strength | tensile strength Break | ISO 527-2/1A/50 | 32.7 MPa |
| elongation | elongation Yield | ASTM D638 | 5.0 % |
| Tensile strain | Tensile strain Yield | ISO 527-2/50 | 4.5 % |
| elongation | elongation Break | ASTM D638 | 21 % |
| Tensile strain | Tensile strain Break | ISO 527-2/50 | 11 % |
| Bending modulus | Bending modulus 50.0mmSpan4 | ASTM D790 | 2500 MPa |
| Bending modulus | Bending modulus 50.0mmSpan5 | ISO 178 | 3180 MPa |
| Tensile modulus | Tensile modulus | ASTM D638 | 2970 MPa |
| thermal performance | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Linear coefficient of thermal expansion | Linear coefficient of thermal expansion MD：-30to100°C | ISO 11359-2 | 5.8E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | Linear coefficient of thermal expansion TD：-30to100°C | ISO 11359-2 | 1.2E-04 cm/cm/°C |
| Hot deformation temperature | Hot deformation temperature 0.45MPa,Unannealed,3.20mm | ASTM D648 | 129 °C |
| Hot deformation temperature | Hot deformation temperature 0.45MPa,Unannealed | ISO 75-2/B | 128 °C |
| Hot deformation temperature | Hot deformation temperature 1.8MPa,Unannealed,3.20mm | ASTM D648 | 73.0 °C |
| Hot deformation temperature | Hot deformation temperature 1.8MPa,Unannealed | ISO 75-2/A | 73.0 °C |
| Vicat softening temperature | Vicat softening temperature | ISO 306/A50 | 157 °C |
| Linear coefficient of thermal expansion | Linear coefficient of thermal expansion MD：-30to100°C | ISO 11359-2 | 5.8E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | Linear coefficient of thermal expansion TD：-30to100°C | ISO 11359-2 | 1.2E-04 cm/cm/°C |
| Hot deformation temperature | Hot deformation temperature 1.8MPa,Unannealed | ISO 75-2/A | 73.0 °C |
| Vicat softening temperature | Vicat softening temperature | ISO 306/A50 | 157 °C |
| Hot deformation temperature | Hot deformation temperature 0.45MPa,Unannealed,3.20mm | ASTM D648 | 129 °C |
| Hot deformation temperature | Hot deformation temperature 0.45MPa,Unannealed | ISO 75-2/B | 128 °C |
| Hot deformation temperature | Hot deformation temperature 1.8MPa,Unannealed,3.20mm | ASTM D648 | 73.0 °C |
| Physical properties | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| density | density | ASTM D792 | 1.05 g/cm³ |
| density | density | ISO 1183 | 1.05 g/cm³ |
| melt mass-flow rate | melt mass-flow rate 230°C/2.16kg | ISO 1133 | 19 g/10min |
| Shrinkage rate | Shrinkage rate TD:23°C,48hr | Internal Method | 1.3 % |
| Shrinkage rate | Shrinkage rate MD:23°C,48hr | Internal Method | 0.95 % |
| density | density | ASTM D792 | 1.05 g/cm³ |
| density | density | ISO 1183 | 1.05 g/cm³ |
| melt mass-flow rate | melt mass-flow rate 230°C/2.16kg | ISO 1133 | 19 g/10min |
| Shrinkage rate | Shrinkage rate TD:23°C,48hr | Internal Method | 1.3 % |
| Shrinkage rate | Shrinkage rate MD:23°C,48hr | Internal Method | 0.95 % |
| hardness | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Shore hardness | Shore hardness ShoreD | ISO 868 | 74 |
| Shore hardness | Shore hardness ShoreD | ISO 868 | 74 |