PP GAPEX® RPP10EU07NA USA Fulu

So sánh

Bảng thông số kỹ thuật

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ASTM D256	75 J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ASTM D4812	480 J/m
Dart impact	Dart impact 23°C	ASTM D5420	0.452 J

impact performance

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Impact strength of cantilever beam gap

23°C

ASTM D256

75 J/m

Impact strength of cantilever beam gap

23°C

ASTM D4812

480 J/m

Dart impact

23°C

ASTM D5420

0.452 J

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
bending strength	bending strength 23°C	ASTM D790	68.3 MPa
tensile strength	tensile strength 23°C	ASTM D638	45.5 MPa
elongation	elongation Break,23°C	ASTM D638	4.0 %
Bending modulus	Bending modulus 1%Secant:23°C	ASTM D790	2160 MPa
Bending modulus	Bending modulus	Bending modulus Tangent:23°C	ASTM D790	2210 MPa
elongation	elongation Break, 23℃	ASTM D638	4.0 %
Bending modulus	Bending modulus 1% Secant: 23℃	ASTM D790	2160 MPa
Bending modulus	Bending modulus	Bending modulus Tangent: 23℃	ASTM D790	2210 MPa
bending strength	bending strength 23℃	ASTM D790	68.3 MPa
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23℃	ASTM D256	75 J/m
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength 23℃	ASTM D4812	480 J/m
Dart impact	Dart impact 23℃	ASTM D5420	0.452 J
tensile strength	tensile strength 23℃	ASTM D638	45.5 MPa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed	ASTM D648	154 °C
	Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed	ASTM D648	129 °C
		Hot deformation temperature	Hot deformation temperature 0.45 MPa, Unannealed	ASTM D648	154 ℃
		Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.8 MPa, Unannealed	ASTM D648	129 ℃

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
density	density	ASTM D792	0.968 g/cm³
melt mass-flow rate	melt mass-flow rate 230°C/2.16kg	ASTM D1238	6.5 g/10min
density	density	ASTM D792	0.968 g/cm3
Shrinkage rate	Shrinkage rate MD	ASTM D955	0.70 %
Shrinkage rate	Shrinkage rate	Shrinkage rate TD	ASTM D955	1.0 %
melt mass-flow rate	melt mass-flow rate 230℃/2.16 kg	ASTM D1238	6.5 g/10min
Shrinkage rate	Shrinkage rate MD	ASTM D955	0.7 %
Shrinkage rate	Shrinkage rate	Shrinkage rate TD	ASTM D955	1.0 %

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.