PA612 VESTAMID® D DX9305 Altuglas International of Arkema Inc.

So sánh

Bảng thông số kỹ thuật

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch 23°C	ISO 179/1eU	NoBreak
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch -30°C	ISO 179/1eU	NoBreak
Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C,Complete Break	ISO 179/1eA	6.0 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	Charpy Notched Impact Strength -30°C,Complete Break	ISO 179/1eA	6.0 kJ/m²

flammability	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
UL flame retardant rating	UL flame retardant rating 1.6mm	UL 94	HB
UL flame retardant rating	UL flame retardant rating 3.2mm	UL 94	HB

flammability

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

UL flame retardant rating

1.6mm

UL 94

UL flame retardant rating

3.2mm

UL 94

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Tensile strain	Tensile strain Break	ISO 527-2/1A	>50 %
Tensile strain	Tensile strain	Tensile strain Yield	ISO 527-2/1A	4.3 %
tensile strength	tensile strength Yield	ISO 527-2/1A	60.0 MPa
Tensile modulus	Tensile modulus	ISO 527-2/1A	2250 MPa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed	ISO 75-2/B	175 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed3	ISO 75-2/B	185 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD：23to55°C	ISO 11359-2	1.4E-04 cm/cm/°C
Melting temperature	Melting temperature	ISO 11357-3	213 °C
Vicat softening temperature	Vicat softening temperature	ISO 306/B	185 °C
Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed	ISO 75-2/A	60.0 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed7	ISO 75-2/A	70.0 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Water absorption rate	Water absorption rate Equilibrium,23°C,50%RH	ISO 62	1.0 %
Water absorption rate	Water absorption rate	Water absorption rate Saturation,23°C	ISO 62	2.7 %
Shrinkage rate	Shrinkage rate MD	ISO 294-4	1.8 %
Shrinkage rate	Shrinkage rate	Shrinkage rate TD	ISO 294-4	1.2 %
density	density 23°C	ISO 1183	1.06 g/cm³

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Relative permittivity	Relative permittivity 100Hz	IEC 60250	4.30
Relative permittivity	Relative permittivity	Relative permittivity 1MHz	IEC 60250	3.30
Dielectric strength	Dielectric strength	IEC 60243-1	23 kV/mm
Volume resistivity	Volume resistivity	IEC 60093	1E+13 ohms·cm
Dissipation factor	Dissipation factor 100Hz	IEC 60250	0.055
Dissipation factor	Dissipation factor	Dissipation factor 1MHz	IEC 60250	0.032
Compared to the anti leakage trace index	Compared to the anti leakage trace index SolutionA	IEC 60112	PLC 0

Supplementary Information	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
ISO Shortcut	ISO Shortcut	ISO 1874	PA612,EHL,22-020
Electrolytic corrosion	Electrolytic corrosion	IEC 60426	AN1.2

Supplementary Information

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

ISO Shortcut

ISO 1874

PA612,EHL,22-020

Electrolytic corrosion

IEC 60426

AN1.2

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.