PPO FLEX NORYL™ GFN1630V-801 SABIC INNOVATIVE NETHERLANDS

131

Đặc tính:
Chịu nhiệt độ caoChống thủy phân
Lĩnh vực ứng dụng:
Phụ tùng ô tôVỏ máy tính xách tay
So sánh

Bảng thông số kỹ thuật

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch -30°C	ISO 179/1eU	33 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch 23°C	ISO 179/1eU	35 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap -30°C	ISO 180/1A	9.4 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ISO 180/1A	11 kJ/m²
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength -30°C	ISO 180/1U	25 kJ/m²
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength 23°C	ISO 180/1U	28 kJ/m²
Dart impact	Dart impact 23°C,TotalEnergy	ASTM D3763	21.7 J

flammability	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
UL flame retardant rating	UL flame retardant rating 1.5mm	UL 94	HB

flammability

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

UL flame retardant rating

1.5mm

UL 94

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Tensile modulus	Tensile modulus	ASTM D638	4350 Mpa
Tensile modulus	Tensile modulus	Tensile modulus	ISO 527-2/1	4400 Mpa
tensile strength	tensile strength Break	ASTM D638	63.0 Mpa
tensile strength	tensile strength	tensile strength Break	ISO 527-2	64.0 Mpa
elongation	elongation Break	ASTM D638	3.0 %
Tensile strain	Tensile strain Break	ISO 527-2	3.0 %
Bending modulus	Bending modulus 50.0mmSpan4	ASTM D790	3840 Mpa
	Bending modulus	Bending modulus 100mmSpan5	ASTM D790	3590 Mpa
	Bending modulus	Bending modulus	Bending modulus	ISO 178	4160 Mpa
bending strength	bending strength	ISO 178	122 Mpa
	bending strength	bending strength Yield,50.0mmSpan4	ASTM D790	116 Mpa
	bending strength	bending strength	bending strength Yield,100mmSpan5	ASTM D790	108 Mpa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
RTI Elec	RTI Elec	UL 746	90.0 °C
RTI Imp	RTI Imp	UL 746	90.0 °C
RTI Str	RTI Str	UL 746	90.0 °C
Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed,3.20mm	ASTM D648	131 °C
	Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed,100mmSpan	ISO 75-2/Be	132 °C
		Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed,3.20mm	ASTM D648	122 °C
			Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed,6.40mm	ASTM D648	125 °C
			Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed,100mmSpan	ISO 75-2/Ae	124 °C
Vicat softening temperature	Vicat softening temperature --	ISO 306/B50	131 °C
Vicat softening temperature	Vicat softening temperature	Vicat softening temperature --	ISO 306/B120	134 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD：-40to40°C	ASTME831	5.1E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD：-40to40°C	ASTME831	7.1E-05 cm/cm/°C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
melt mass-flow rate	melt mass-flow rate 300°C/5.0kg	ASTM D1238	17 g/10min
Melt Volume Flow Rate (MVR)	Melt Volume Flow Rate (MVR) 300°C/5.0kg	ISO 1133	16.4 cm3/10min
Shrinkage rate	Shrinkage rate MD：3.20mm	Internal Method	0.20-0.50 %
Water absorption rate	Water absorption rate 24hr	ASTM D570	0.060 %
Outdoor applicability	Outdoor applicability	UL 746C	f1

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Dielectric constant	Dielectric constant 1MHz	ASTM D150	2.90
Dissipation factor	Dissipation factor 1MHz	ASTM D150	1.4E-03
Arc resistance	Arc resistance	ASTM D495	PLC7
High arc combustion index	High arc combustion index HAI	UL 746	PLC 4
High voltage arc tracing rate	High voltage arc tracing rate HVTR	UL 746	PLC 4
Hot wire ignition	Hot wire ignition HWI	UL 746	PLC 5

hardness	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Rockwell hardness	Rockwell hardness L-Sale	ASTM D785	104

hardness

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Rockwell hardness

L-Sale

ASTM D785

104

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.