PET UmaPET ULM Ester Industries Ltd.

So sánh

Bảng thông số kỹ thuật

optical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Apparent density	Apparent density 23.0μm	Internal Method	-2.8-7.2 %
Apparent density	Apparent density 15.0μm	Internal Method	-2.8-7.2 %
Apparent density	Apparent density 12.0μm	Internal Method	-2.8-7.2 %

optical performance

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Apparent density

23.0μm

Internal Method

-2.8-7.2 %

Apparent density

15.0μm

Internal Method

-2.8-7.2 %

Apparent density

12.0μm

Internal Method

-2.8-7.2 %

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
surface strength	surface strength 23.0μm，金属化面	ASTM D2578	56 mN/m
Shrinkage rate	Shrinkage rate MD:150°C,30分钟,0.0150mm	ASTM D1204	2.5 %
	Shrinkage rate	Shrinkage rate MD:150°C,30分钟,0.0120mm	ASTM D1204	2.5 %
		Shrinkage rate	Shrinkage rate MD:150°C,30分钟,0.0230mm	ASTM D1204	2.5 %
			Shrinkage rate	Shrinkage rate TD:150°C,30分钟,0.0120mm	ASTM D1204	0.40 %
				Shrinkage rate	Shrinkage rate TD:150°C,30分钟,0.0150mm	ASTM D1204	0.40 %
				Shrinkage rate	Shrinkage rate	Shrinkage rate TD:150°C,30分钟,0.0230mm	ASTM D1204	0.40 %
surface strength	surface strength 12.0μm，金属化面	ASTM D2578	56 mN/m
surface strength	surface strength	surface strength 15.0μm，金属化面	ASTM D2578	56 mN/m

film	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
film thickness	film thickness		12.15.23µm
film thickness	film thickness	film thickness		121523 µm
elongation	elongation TD:Break,12μm	ASTM D882	90 %
	elongation	elongation MD:Break,23μm	ASTM D882	100 %
		elongation	elongation MD:Break,15μm	ASTM D882	100 %
		elongation	elongation	elongation MD:Break,12μm	ASTM D882	100 %
tensile strength	tensile strength TD:Break,23μm	ASTM D882	206 MPa
	tensile strength	tensile strength TD:Break,15μm	ASTM D882	206 MPa
		tensile strength	tensile strength TD:Break,12μm	ASTM D882	216 MPa
			tensile strength	tensile strength MD:Break,23μm	ASTM D882	186 MPa
			tensile strength	tensile strength	tensile strength MD:Break,15μm	ASTM D882	186 MPa
Water vapor permeability	Water vapor permeability --4	ASTMF1249	0.60 g/m²/24hr
	Water vapor permeability	Water vapor permeability --3	ASTMF1249	0.60 g/m²/24hr
	Water vapor permeability	Water vapor permeability	Water vapor permeability --2	ASTMF1249	0.60 g/m²/24hr
Oxygen permeability	Oxygen permeability 23°C,23μm	ASTM D3985	0.800 cm³/m²/24hr
	Oxygen permeability	Oxygen permeability 23°C,15μm	ASTM D3985	0.800 cm³/m²/24hr
	Oxygen permeability	Oxygen permeability	Oxygen permeability 23°C,12μm	ASTM D3985	0.900 cm³/m²/24hr
elongation	elongation TD:Break,23μm	ASTM D882	90 %
tensile strength	tensile strength MD:Break,12μm	ASTM D882	206 MPa
elongation	elongation TD:Break,15μm	ASTM D882	90 %
consumption	consumption 23.0μm	Internal Method	31.0 m²/kg
	consumption	consumption 12.0μm	Internal Method	59.5 m²/kg
	consumption	consumption	consumption 15.0μm	Internal Method	47.6 m²/kg

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.