HMW-HDPE Marlex® HXM 50100-01 Chevron Phillips Chemical Company LLC

So sánh

Bảng thông số kỹ thuật

	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
elongation	elongation Break,Compression Molded	ASTM D638	750 %
Bending modulus	Bending modulus CompressionMolded，Tangent	ASTM D790	1200 MPa
impact strength	impact strength CompressionMolded	ASTM D1822	170 kJ/m²
Shore hardness	Shore hardness ShoreD,Compression Molded	ASTM D2240	66
Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed,Compression Molded	ASTM D648	69.0 °C
Brittle temperature	Brittle temperature	ASTM D746A	<-75.0 °C
Vicat softening temperature	Vicat softening temperature	ASTM D15255	124 °C
density	density	ASTM D1505	0.948 g/cm³
melt mass-flow rate	melt mass-flow rate 190°C/21.6kg	ASTM D1238	12 g/10min
Environmental stress cracking resistance	Environmental stress cracking resistance 100%Igepal,Compression Molded,F50	ASTM D1693B	>600 hr
tensile strength	tensile strength Yield,Compression Molded	ASTM D638	25.0 MPa

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.