NBR NANCAR® 4155 Nantex Industry Co., Ltd.

So sánh

Bảng thông số kỹ thuật

elastomer	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
tear strength	tear strength	ASTM D624	58.0 kN/m
elongation	elongation Break5	ASTM D412	520 %
	elongation	elongation Break4	ASTM D412	540 %
	elongation	elongation	elongation Break3	ASTM D412	590 %
tensile strength	tensile strength Yield5	ASTM D412	26.0 MPa
	tensile strength	tensile strength Yield4	ASTM D412	26.8 MPa
		tensile strength	tensile strength Yield3	ASTM D412	26.4 MPa
			tensile strength	tensile strength 300%Strain5	ASTM D412	13.3 MPa
				tensile strength	tensile strength 300%Strain4	ASTM D412	12.8 MPa
				tensile strength	tensile strength	tensile strength 300%Strain3	ASTM D412	10.9 MPa
Permanent compression deformation	Permanent compression deformation 100°C,70hr	ASTM D395	59 %

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Heat loss	Heat loss	ASTM D5688	0.30 %

thermal performance

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Heat loss

ASTM D5688

0.30 %

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Soluble inMEK	Soluble inMEK		100 %
stabilizer	stabilizer		Non-staining
bound acrylonitrile content	bound acrylonitrile content	Internal Method	40.0 %
Mooney viscosity	Mooney viscosity ML1+4,100°C2	ASTM D1646	78 MU
Mooney viscosity	Mooney viscosity	Mooney viscosity ML1+4,100°C	ASTM D1646	51 MU
density	density		1.00 g/cm³

hardness	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Shore hardness	Shore hardness ShoreA,5Sec5	ASTM D2240	78
Shore hardness	Shore hardness ShoreA,5Sec4	ASTM D2240	77
Shore hardness	Shore hardness ShoreA,5Sec3	ASTM D2240	76

hardness

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Shore hardness

ShoreA,5Sec5

ASTM D2240

Shore hardness

ShoreA,5Sec4

ASTM D2240

Shore hardness

ShoreA,5Sec3

ASTM D2240

aging	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Change rate of tensile strength in air	Change rate of tensile strength in air 100°C,70hr,在ASTM#1油中	ASTM D471	-11 %
Change rate of hardness (Shore) in the air	Change rate of hardness (Shore) in the air ShoreA,100°C,70hr	ASTM D573	5.0
Change rate of ultimate elongation in air	Change rate of ultimate elongation in air 100°C,70hr	ASTM D573	-22 %
Volume change	Volume change 100°C,70hr,在IRM903油中	ASTM D471	8.5 %
Change rate of tensile strength in air	Change rate of tensile strength in air 100°C,70hr	ASTM D573	-1.0 %
Change rate of tensile strength in air	Change rate of tensile strength in air	Change rate of tensile strength in air 100°C,70hr,在IRM903油中	ASTM D471	-26 %
Change rate of ultimate elongation in air	Change rate of ultimate elongation in air 100°C,70hr,在ASTM#1油中	ASTM D471	-28 %
Change rate of ultimate elongation in air	Change rate of ultimate elongation in air	Change rate of ultimate elongation in air 100°C,70hr,在IRM903油中	ASTM D471	-28 %
Change rate of hardness (Shore) in the air	Change rate of hardness (Shore) in the air 支撐A,100°C,70hr,在ASTM#1油中	ASTM D471	3.0
Change rate of hardness (Shore) in the air	Change rate of hardness (Shore) in the air	Change rate of hardness (Shore) in the air 支撐A,100°C,70hr,在IRM903油中	ASTM D471	-5.0
Volume change	Volume change 100°C,70hr,ASTM标准油（1号）	ASTM D471	-0.20 %

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.