PP POLYfill PP EQX10030R UV POLYKEMI SWEDEN

So sánh

Bảng thông số kỹ thuật

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C	ISO 179	6.0 kJ/m²
	Charpy Notched Impact Strength	Charpy Notched Impact Strength -20°C	ISO 179	3.0 kJ/m²
		Charpy Notched Impact Strength	Charpy Notched Impact Strength -20°C	ISO 179	3.0 kJ/m²
		Charpy Notched Impact Strength	Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C	ISO 179	6.0 kJ/m²

flammability	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
UL flame retardant rating	UL flame retardant rating 1.6mm	UL 94	HB
Hot filament ignition temperature	Hot filament ignition temperature 2.0mm	IEC 60695-2-13	750 °C
UL flame retardant rating	UL flame retardant rating 1.6mm	UL 94	HB
Hot filament ignition temperature	Hot filament ignition temperature 2.0mm	IEC 60695-2-13	750 °C

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
tensile strength	tensile strength	ISO 527-2	21.0 MPa
Tensile strain	Tensile strain Break	ISO 527-2	9.0 %
tensile strength	tensile strength	ISO 527-2	21.0 MPa
Tensile strain	Tensile strain Break	ISO 527-2	9.0 %
Bending modulus	Bending modulus 23°C	ISO 178	2200 MPa
bending strength	bending strength	ISO 178	36.0 MPa
Bending modulus	Bending modulus 23°C	ISO 178	2200 MPa
bending strength	bending strength	ISO 178	36.0 MPa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed	ISO 75-2/B	139 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed	ISO 75-2/A	76.0 °C
Vicat softening temperature	Vicat softening temperature --	ISO 306/A50	144 °C
	Vicat softening temperature	Vicat softening temperature --	ISO 306/B50	63.0 °C
		Vicat softening temperature	Vicat softening temperature --	ISO 306/A50	144 °C
		Vicat softening temperature	Vicat softening temperature	Vicat softening temperature --	ISO 306/B50	63.0 °C
Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed	ISO 75-2/B	139 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed	ISO 75-2/A	76.0 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
density	density	ISO 1183	1.12 g/cm³
melt mass-flow rate	melt mass-flow rate 230°C/2.16kg	ISO 1133	10 g/10min
density	density	ISO 1183	1.12 g/cm³
melt mass-flow rate	melt mass-flow rate 230°C/2.16kg	ISO 1133	10 g/10min

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.