mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Tensile modulus	Tensile modulus 23°C	ISO 527-2	2150 Mpa
tensile strength	tensile strength 23°C	ISO 527-2	40.0 Mpa
Bending modulus	Bending modulus 23°C	ISO 178	2230 Mpa
bending strength	bending strength 23°C	ISO 178	65.0 Mpa
tensile strength	tensile strength 23℃	ISO 527-2	40.0 Mpa
Bending modulus	Bending modulus 23℃	ISO 178	2230 Mpa
bending strength	bending strength 23℃	ISO 178	65.0 Mpa
Charpy Notched Impact Strength	Charpy Notched Impact Strength -30℃	ISO 179	3.0 kJ/m²
Rockwell hardness	Rockwell hardness 23℃	ISO 2039-2	100 R 计秤
Tensile modulus	Tensile modulus 23℃	ISO 527-2	2150 Mpa
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	ASTM D256/ISO 179	3 kg·cm/cm(J/M)ft·lb/in
Tensile modulus	Tensile modulus	ASTM D638/ISO 527	2150 kg/cm²(MPa)[Lb/in²]
tensile strength	tensile strength	ASTM D638/ISO 527	40 kg/cm²(MPa)[Lb/in²]
Rockwell hardness	Rockwell hardness	ASTM D785	100
Bending modulus	Bending modulus	ASTM D790/ISO 178	2230 kg/cm²(MPa)[Lb/in²]
bending strength	bending strength	ASTM D790/ISO 178	65 kg/cm²(MPa)[Lb/in²]
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	ASTM D256/ISO 179	6 kg·cm/cm(J/M)ft·lb/in

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed	ISO 75-2/Af	105 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD	ISO 11359-2	8E-05 cm/cm/°C
Hot deformation temperature	Hot deformation temperature 1.80MPa，Unannealed	ISO 75-2/Af	105 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion Flow	ISO 11359-2	0.000080 cm/cm/℃
UL flame retardant rating	UL flame retardant rating	UL 94	V-0
Combustibility (rate)	Combustibility (rate)	UL 94	1.5 V-0
Hot deformation temperature	Hot deformation temperature HDT	ASTM D648/ISO 75	105 ℃（℉）
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	ASTM D696/ISO 11359	8 mm/mm.℃

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Melt Volume Flow Rate (MVR)	Melt Volume Flow Rate (MVR) 220°C/10.0kg	ISO 1133	2.00 cm3/10min
Shrinkage rate	Shrinkage rate MD：23°C	ISO 294-4	0.60-0.80 %
Melt Volume Flow Rate (MVR)	Melt Volume Flow Rate (MVR) 220℃/2.16 kg	ISO 1133	2.00 cm3/10min
Shrinkage rate	Shrinkage rate MD，23℃	ISO 294-4	0.60 - 0.80 %
density	density	ASTM D792/ISO 1183	1.21
Shrinkage rate	Shrinkage rate	ASTM D955	0.6-0.8 %
melt mass-flow rate	melt mass-flow rate	ASTM D1238/ISO 1133	2 g/10min

hardness	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Rockwell hardness	Rockwell hardness R-Sale,23°C	ISO 2039-2	100

hardness

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Rockwell hardness

R-Sale,23°C

ISO 2039-2

100

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.