mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Charpy Notched Impact Strength	Charpy Notched Impact Strength -30℃	ISO 179/1eA	4.5 KJ/m
Charpy Notched Impact Strength	Charpy Notched Impact Strength	Charpy Notched Impact Strength 23℃	ISO 179/1eA	5.00 KJ/m
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch -30℃	ISO 179/1eU	190 KJ/m
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch 23℃	ISO 179/1eU	200 KJ/m
Rockwell hardness	Rockwell hardness	ISO 868	79 D
Ball Pressure Test	Ball Pressure Test	ISO 2039-1	160 Mpa
Tensile modulus	Tensile modulus	ISO 527-2	2600 Mpa
tensile strength	tensile strength Yield	ISO 527-2	55 Mpa
Tensile strain	Tensile strain Yield	ISO 527-2	4.0 %
Tensile strain	Tensile strain	Tensile strain Break	ISO 527-2	50 %

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot deformation temperature	Hot deformation temperature 0.45Mpa,Unannealed	ISO 75-2/B	150 ℃
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.8Mpa,Unannealed	ISO 75-2/B	55 ℃
Vicat softening temperature	Vicat softening temperature -	ISO 306/A	220 ℃
Vicat softening temperature	Vicat softening temperature	Vicat softening temperature -	ISO 306/B	180 ℃
UL flame retardant rating	UL flame retardant rating 0.8mm	UL94	HB
UL flame retardant rating	UL flame retardant rating	UL flame retardant rating 1.6mm	UL94	HB

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
density	density	ISO 1183	1.31
melt mass-flow rate	melt mass-flow rate 250℃/2.16kg	ISO 1133	45 cm
Shrinkage rate	Shrinkage rate 80℃	ISO 294-4	1.5 %
Water absorption rate	Water absorption rate	ISO 62	0.45 %

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Compared to the Leakage Traceability Index (CTI)	Compared to the Leakage Traceability Index (CTI) -	IEC 60112	575 V
Compared to the Leakage Traceability Index (CTI)	Compared to the Leakage Traceability Index (CTI)	Compared to the Leakage Traceability Index (CTI) -	IEC 60112	600 V
Dielectric strength	Dielectric strength	IEC 60243-1	27 KV/mm
Surface resistivity	Surface resistivity	IEC 60093	1E+13 Ohms
Volume resistivity	Volume resistivity	IEC 60093	1E+15 Ohm.cm
	Volume resistivity	Volume resistivity 23℃,100Hz	IEC 60250	3.3
	Volume resistivity	Volume resistivity	Volume resistivity 23℃,1E+6Hz	IEC 60250	3.5
Dielectric loss	Dielectric loss 23℃,100Hz	IEC 60250	0.002
Dielectric loss	Dielectric loss	Dielectric loss 23℃,1E+6Hz	IEC 60250	0.023

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.