PEI+PCE ULTEM™ AUT195 resin SABIC

So sánh

Bảng thông số kỹ thuật

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ASTM D256	53 J/m
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap -30°C	ISO 180/1A	5.0 kJ/m²
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ISO 180/1A	5.0 kJ/m²
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ASTM D4812	2100 J/m
Charpy Notched Impact Strength	Charpy Notched Impact Strength -30°C	ISO 179/1eA	4.0 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C	ISO 179/1eA	4.0 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 3.20mm	ASTM D256	2100 J/m

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
elongation	elongation Break	ASTM D638	70 %
Bending modulus	Bending modulus 100mmSpan	ASTM D790	3170 MPa
Bending modulus	Bending modulus	Bending modulus	ISO 178	3100 MPa
bending strength	bending strength Yield,100mmSpan	ASTM D790	145 MPa
Tensile modulus	Tensile modulus	ISO 527-2/1	3000 MPa
tensile strength	tensile strength Yield	ASTM D638	96.5 MPa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD：23to150°C	ISO 11359-2	6E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD：23to150°C	ISO 11359-2	6E-05 cm/cm/°C
thermal conductivity	thermal conductivity	ISO 8302	0.23 W/m/K
Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed,100mmSpan	ISO 75-2/Be	195 °C
	Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed,6.40mm	ASTM D648	190 °C
	Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed,100mmSpan	ISO 75-2/Ae	180 °C
Vicat softening temperature	Vicat softening temperature	ISO 306/B120	205 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
density	density	ASTM D792	1.26 g/cm³
density	density	density	ISO 1183	1.27 g/cm³
melt mass-flow rate	melt mass-flow rate 337°C/6.6kg	ASTM D1238	24 g/10min
Melt Volume Flow Rate (MVR)	Melt Volume Flow Rate (MVR) 340°C/5.0kg	ISO 1133	16.0 cm³/10min
Shrinkage rate	Shrinkage rate MD：3.20mm	Internal Method	0.50to0.70 %
Shrinkage rate	Shrinkage rate	Shrinkage rate TD2	Internal Method	0.50to0.70 %
Water absorption rate	Water absorption rate Saturation,23°C	ISO 62	0.90 %
Water absorption rate	Water absorption rate	Water absorption rate Equilibrium,23°C,50%RH	ISO 62	0.50 %

Supplementary Information	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Metallic haze	Metallic haze 起始	Internal Method	195 °C

Supplementary Information

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Metallic haze

起始

Internal Method

195 °C

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.