PBT+PET POCAN® ECO T 3220 000000 LANXESS GERMANY
So sánhBảng thông số kỹ thuật
| impact performance | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Impact strength of simply supported beam without notch | Impact strength of simply supported beam without notch 23°C | ISO 179/1eU | 40 kJ/m² |
| Impact strength of simply supported beam without notch | Impact strength of simply supported beam without notch -30°C | ISO 179/1eU | 35 kJ/m² |
| Charpy Notched Impact Strength | Charpy Notched Impact Strength 23°C | ISO 179/1eA | <10 kJ/m² |
| Charpy Notched Impact Strength | Charpy Notched Impact Strength -30°C | ISO 179/1eA | <10 kJ/m² |
| Suspended wall beam without notch impact strength | Suspended wall beam without notch impact strength 23°C | ISO 180/1U | 35 kJ/m² |
| Suspended wall beam without notch impact strength | Suspended wall beam without notch impact strength -30°C | ISO 180/1U | 35 kJ/m² |
| Impact strength of cantilever beam gap | Impact strength of cantilever beam gap 23°C | ISO 180/1A | <10 kJ/m² |
| Impact strength of cantilever beam gap | Impact strength of cantilever beam gap -30°C | ISO 180/1A | <10 kJ/m² |
| mechanical properties | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| bending strength | bending strength FlexuralStrainatFlexuralStrength5(23°C) | 3.5 % | |
| bending strength | bending strength 23°C | ISO 178 | 195 MPa |
| Tensile modulus | Tensile modulus 23°C | ISO 527-2/1 | 7500 MPa |
| tensile strength | tensile strength Break,23°C | ISO 527-2/5 | 120 MPa |
| Tensile strain | Tensile strain Break,23°C | ISO 527-2/5 | 3.2 % |
| Bending modulus | Bending modulus 23°C | ISO 178/A | 7500 MPa |
| bending strength | bending strength 3.5%Strain | ISO 178/A | 195 MPa |
| thermal performance | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Melting temperature | Melting temperature | ISO 11357-3 | 225to250 °C |
| Vicat softening temperature | Vicat softening temperature | ISO 306/B120 | 210 °C |
| Hot deformation temperature | Hot deformation temperature 1.8MPa,Unannealed | ISO 75-2/A | 195 °C |
| Hot deformation temperature | Hot deformation temperature 0.45MPa,Unannealed | ISO 75-2/B | 220 °C |
| Linear coefficient of thermal expansion | Linear coefficient of thermal expansion TD：23to55°C | ISO 11359-2 | 9E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | Linear coefficient of thermal expansion MD：23to55°C | ISO 11359-2 | 3E-05 cm/cm/°C |
| Physical properties | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Shrinkage rate | Shrinkage rate MD:120°C,2hr,2.00mm3 | ISO 294-4 | 0.10 % |
| Shrinkage rate | Shrinkage rate MD:270°C,2.00mm2 | ISO 294-4 | 0.40 % |
| Shrinkage rate | Shrinkage rate TD:120°C,2hr,2.00mm3 | ISO 294-4 | 0.20 % |
| Shrinkage rate | Shrinkage rate TD:270°C,2.00mm2 | ISO 294-4 | 1.0 % |
| Melt Volume Flow Rate (MVR) | Melt Volume Flow Rate (MVR) 260°C/2.16kg | ISO 1133 | 15.0 cm³/10min |
| Apparent density | Apparent density | ISO 60 | 0.80 g/cm³ |
| density | density 23°C | ISO 1183 | 1.47 g/cm³ |
| Water absorption rate | Water absorption rate Saturation,23°C | ISO 62 | 0.40 % |
| Water absorption rate | Water absorption rate Equilibrium,23°C,50%RH | ISO 62 | 0.20 % |
| Electrical performance | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Compared to the anti leakage trace index | Compared to the anti leakage trace index SolutionA | IEC 60112 | PLC 2 |
| Supplementary Information | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| ISO Shortcut | ISO Shortcut | ISO 7792 | PBT+PET.GHMR.09-070.GF20 |