mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
tensile strength	tensile strength Yield	ASTM D638	138 MPa
tensile strength	tensile strength	tensile strength Break	ASTM D638	110 MPa
elongation	elongation Yield	ASTM D638	4.0 %
Bending modulus	Bending modulus	ASTM D790	4550 MPa
bending strength	bending strength 5.0%Strain	ASTM D790	193 MPa
compressive strength	compressive strength	ASTM D695	207 MPa
shear strength	shear strength	ASTM D732	138 MPa
elongation	elongation Break	ASTM D638	12 %
Tensile modulus	Tensile modulus	ASTM D638	4410 MPa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed	ASTM D648	175 °C
Glass transition temperature	Glass transition temperature	DSC	163 °C
Melting temperature	Melting temperature	DSC	360 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD	ASTM D696	2.1E-05 cm/cm/°C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
density	density	ASTM D792	1.31 g/cm³
melt mass-flow rate	melt mass-flow rate 400°C/8.4kg	ASTM D1238	100to120 g/10min
Shrinkage rate	Shrinkage rate MD	ASTM D955	1.4 %
Water absorption rate	Water absorption rate 24hr	ASTM D570	<0.20 %

hardness	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Rockwell hardness	Rockwell hardness M-Scale	ASTM D785	88

hardness

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Rockwell hardness

M-Scale

ASTM D785

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.