XLPE Pexidan® R/T USA Saco Polymers

So sánh

Bảng thông số kỹ thuật

	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
HotElongation	HotElongation 150°C	Internal Method	40 %
tensile strength	tensile strength Yield	CSA22.2No.38	12.4 MPa
Crosslinking degree	Crosslinking degree	ASTM D2765	72 %
melt mass-flow rate	melt mass-flow rate 190°C/2.16kg	ASTM D1238	0.80 g/10min
density	density	ASTM D792	0.918 g/cm³
tensile strength	tensile strength Break2	ASTM D638	15.9 MPa
tensile strength	tensile strength	tensile strength Break	CSA22.2No.38	16.5 MPa
insulation resistance	insulation resistance after12weeks:90°C	CSA22.2No.38	2.09E+10 Mohms/km
insulation resistance	insulation resistance	insulation resistance 15°C	CSA22.2No.38	1.15E+10 Mohms/km
Dissipation factor	Dissipation factor 100MHz	ASTM D150	4.6E-04
Dissipation factor	Dissipation factor	Dissipation factor 1MHz	ASTM D150	4.4E-04
Dielectric constant	Dielectric constant 60Hz	CSA22.2No.38	2.38
	Dielectric constant	Dielectric constant 100MHz	ASTM D150	2.28
	Dielectric constant	Dielectric constant	Dielectric constant 1MHz	ASTM D150	2.28
deformation	deformation	CSA22.2No.38	5.0 %
Brittle temperature	Brittle temperature	ASTM D746	<-75.0 °C
Shrinkback	Shrinkback	CSA22.2No.38	0.00 mm
elongation	elongation Break2	ASTM D638	310 %
elongation	elongation	elongation Break	CSA22.2No.38	340 %

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.